Method of fabricating thermoelectric device

ABSTRACT

The invention provides a method of fabricating a thermoelectric device, whereby a grooved block ( 11 ) composed of n-type thermoelectric semiconductor and a grooved block ( 21 ) composed of p-type thermoelectric semiconductor, provided with a plurality of grooves ( 16, 26 ) formed therein, respectively, at a same pitch and parallel with each other, are formed such that a depthwise portion of respective grooved blocks is left intact, and then, an integrated block ( 3 ) is formed by fitting and adhering together the grooved blocks ( 11, 21 ) composed of the n-type and p-type thermoelectric semiconductors, respectively, filling up gaps in fitting parts with adhesive insulation members. After removing portions of the integrated block ( 3 ), other than the fitting parts where the n-type and p-type thermoelectric semiconductors are fitted to each other, n-type and p-type thermoelectric semiconductor pieces are exposed, and by forming electrodes for connecting the pieces to each other alternately and in series, the thermoelectric device is completed. Further, it is preferable to apply a process of exposing the thermoelectric semiconductor pieces and a process of forming the electrodes after applying a process of forming grooves to the integrated block ( 3 ) such that a plurality of grooves are formed in the direction crossing the direction in which the grooves ( 16, 26 ) have been formed, leaving a depthwise portion of the integrated block ( 3 ) intact, and insulation members filling up the grooves thus formed are solidified.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method of fabricating athermoelectric device for use in a thermoelectric power generator takingadvantage of the Seebeck effect, or a cooler taking advantage of thePeltier effect, and more particularly, to a method of fabricating asmall sized thermoelectric device incorporating a plurality ofthermocouples.

2. Description of the Related Art

In each of the thermocouples making up a thermoelectric device, avoltage is developed by providing a difference in temperature betweenthe opposite ends thereof. This is due to the effect of the Seebeckeffect, and a device designed to extract the voltage as electric energyis a thermoelectric power generator. The thermoelectric power generatorwherein heat energy can be converted directly into electric energy hasattracted much attention as effective means of utilizing heat energy, asrepresented by the case of waste heat utilization.

Meanwhile, the flow of a current caused to occur through a thermocoupleresults in generation of heat at one end thereof, and absorption of heatat the other end thereof. This is due to the Peltier effect, and acooler can be manufactured by taking advantage of such phenomenon ofheat absorption. This type of cooler which does not comprise mechanicalcomponents and can be reduced in size has an application as a portablerefrigerator, or a localized cooler for lasers, integrated circuits, andthe like.

Thus, the thermoelectric power generator or cooler made up of thethermoelectric device is simple in construction, and is in a morefavorable condition for miniaturization as compared with other types ofpower generators or coolers, offering high usefulness. For example, withthe thermoelectric device for use in the thermoelectric power generator,there will not arise a problem of leakage or depletion of electrolyte aswith the case of a redox cell, and the thermoelectric device hastherefore promising prospects for application to portable electronicdevices such as an electronic wrist watch.

The general construction of a conventional thermoelectric device, and aconventional method of fabricating the same, have been disclosed in, forexample, Japanese Patent Laid-open Publication No. 63-20880 or JapanesePatent Laid-open Publication No. 8-43555. The descriptions disclosedtherein are concerned with a thermoelectric device for use in generationof power. However, the basic construction thereof is the same as that ofa thermoelectric device for use in cooling. Hence, the thermoelectricdevice for use only in generation of power is described hereinafter toavoid complexity in explanation.

In the conventional thermoelectric device disclosed in the publicationsdescribed above, p-type and n-type thermoelectric semiconductors arealternately and regularly arranged so that a multitude of thermocouplesare formed on a horizontal plane, and the thermocouples thus formed areelectrically connected to each other in series.

The thermoelectric device is formed in a sheet-like shape by disposingthe thermocouples on a plane, and the upper surface and under surface ofthe thermoelectric device become faces on which hot junctions and coldjunctions of the thermocouples are located, respectively. Generation ofelectric power in the thermoelectric device is caused to occur by adifference in temperature between the upper surface and the undersurface of the device having a sheet-like shape.

Meanwhile, an output voltage of a thermocouple using a BiTe-basedmaterial, said to have the highest figure of merit of thermoelectricpower generation at present, is about 400 μV/° C. per couple.

When such thermocouples as described above are employed in a portableelectronic device for use at around room temperature, for example, in anelectronic watch, a satisfactory difference in temperature can not beexpected to be developed inside the device. For example, in the case ofa wrist watch, the temperature difference in a wrist watch developedbetween body temperature and the ambient temperature will be 2° C. atmost.

It follows that not less than about 2000 couples of BiTe-basedthermocouples are required to obtain a voltage not lower than 1.5V,necessary for driving an electronic watch.

Furthermore, in the case of an electronic wrist watch, whereinmechanical components and electric circuit components need to be encasedtherein in spite of a small internal volume thereof in the first place,it is required that a thermoelectric device for power generation, verysmall in size, be used.

The conventional method of fabricating a thermoelectric device small insize and composed of a multitude of thermocouples has been disclosed inJapanese Patent Laid-open Publication No. 63-20880.

In the method disclosed, a multi-layered body is formed by stackingp-type and n-type thermoelectric semiconductors, in a thin sheet-likeshape, on top of each other in layers while interposing a heatinsulating material between respective layers, and then by bonding themtogether. Subsequently, grooves are formed at a given spacing in themulti-layered body, whereupon the grooves are filled up with a heatinsulating material, and connecting portions of individualthermoelectric semiconductors are removed, thereby forming n-type andp-type thermocouples, surrounded by the heat insulating material andisolated from each other. By electrically connecting the thermocoupleswith each other in series, a thermoelectric device is completed.

Then, in the method disclosed in Japanese Patent Laid-open PublicationNo. 8-43555, p-type and n-type thermoelectric semiconductors, eachhaving a plate-like shape, are first bonded to separate substrates, andthereafter, a grooving process of forming a multitude of grooves at verysmall spacings in the longitudinal and transverse directions is appliedto respective thermoelectric semiconductors.

As a result of the grooving process described above, a multitude ofthermoelectric semiconductors, each columnar in shape, and upstandingregularly on top of the respective substrates, resembling a kenzan (aneedle-point flower holder for flower arrangement), are formed. Thekenzan-like bodies composed of the n-type and p-type thermoelectricsemiconductors, respectively, are thus prepared, and joined togethersuch that the respective thermoelectric semiconductors, columnar inshape, are mated with each other. Thereafter, an insulating material isfilled between the respective thermoelectric semiconductors.

In the final step of processing, the substrates are removed, and athermoelectric device is completed by electrically connectingthermocouples with each other in series.

However, with the methods of fabricating the thermoelectric device asdescribed in the foregoing, there will arise a problem that the materialused for the thermoelectric semiconductors is prone to breakage duringthe process of forming the thermoelectric semiconductors into asheet-like shape, during the grooving process of forming the kenzan-likebodies, and the like, because of the fragile nature of the materialitself for the thermoelectric semiconductors.

In particular, for forming as many as not less than 2000 couples ofthermocouples in an ultra-small sized thermoelectric device which can beencased in a wrist watch, it is required that the thickness of therespective sheet-like thermoelectric semiconductors or the diameter ofthe respective columnar thermoelectric semiconductors be set to on theorder of 100 μm or less, and consequently, the problem of fragilitydescribed above will become quite serious.

SUMMARY OF THE INVENTION

The present invention has been developed in order to solve such problemsas encountered with the conventional methods of fabricating thethermoelectric device, and an object of the invention is therefore toprovide a method of fabricating with ease and efficiently athermoelectric device small in size, but incorporating a multitude ofthermocouples so as to be able to output a high voltage.

To this end, a method of fabricating a thermoelectric device accordingto the invention comprises:

a grooved block fabrication process of forming grooved blocks composedof an n-type thermoelectric semiconductor and p-type thermoelectricsemiconductor, respectively, each provided with a plurality of groovesformed at a same pitch and parallel with each other, leaving a depthwiseportion of respective grooved blocks intact;

a fitting process of fitting the grooved blocks composed of the n-typethermoelectric semiconductor and p-type thermoelectric semiconductorformed, respectively, by said grooved block fabrication process to eachother such that surfaces of the respective grooved blocks, with thegrooves formed thereon, face each other;

an adhesion process of forming an integrated block by adhering thegrooved block composed of the n-type thermoelectric semiconductor andthe grooved block composed of p-type thermoelectric semiconductor,fitted to each other by said fitting process, to each other afterfilling up gaps in fitting parts between the respective grooved blockswith an adhesive insulation member; and

a thermoelectric semiconductor pieces exposure process of exposingn-type and p-type thermoelectric semiconductor pieces by removing allportions of the integrated block formed by said adhesion process, otherthan the fitting parts where the grooved block composed of the n-typethermoelectric semiconductor and the grooved block composed of p-typethermoelectric semiconductor are fitted to each other.

When fabricating the thermoelectric device by the method comprising theprocess described above, a thermoelectric semiconductor material havinga problem of fragility is always handled in the form of a unit (block).Hence, delicate processing can be applied to the thermoelectricsemiconductor material without causing breakage thereof, enabling thethermoelectric device made up of a plurality of thermocouples composedof a plurality of thermoelectric semiconductor pieces very small in sizeto be efficiently fabricated with ease.

Further, it is preferable that the method according to the inventionfurther comprises a second grooving process of forming a plurality ofgrooves in the integrated block formed by the adhesion process, in thedirection crossing the direction of the grooves formed by said groovedblock fabrication process, leaving a depthwise portion of the integratedblock intact; a solidification process of filling the grooves formed bythe second grooving process with adhesive insulation members andsolidifying the same; and, a thermoelectric semiconductor piecesexposure process, to be applied thereafter, of exposing n-type andp-type thermoelectric semiconductor pieces by removing all portions ofthe integrated block wherein the adhesive insulation members filling upthe grooves are solidified in the solidification process, other than thefitting parts where the grooved blocks composed of the n-typethermoelectric semiconductor and p-type thermoelectric semiconductor,respectively, are fitted to each other.

This will result in a considerable increase in the number ofthermocouples making up a thermoelectric device of a same size, and theoutput voltage of the thermoelectric device when used for generation ofpower can be raised.

It is yet further preferable that the method according to the inventionfurther comprises a grooving process of forming two grooved integratedblocks by forming a plurality of grooves at a same pitch and in thedirection crossing the direction of the grooves formed by the groovedblock fabrication process, leaving a depthwise portion of respectiveintegrated blocks intact, in each of the two integrated blocksfabricated by means of the grooved block fabrication process, fittingprocess, and adhesion process described in the foregoing; a secondfitting process of fitting the two grooved integrated blocks to eachother such that surfaces thereof with the grooves formed thereon faceeach other; a second adhesion process of forming a second integratedblock by filling up gaps in fitting parts between the two groovedintegrated blocks fitted to each other by the fitting process withadhesive insulation members, and solidifying the same; and athermoelectric semiconductor pieces exposure process, to be appliedthereafter, of exposing n-type and p-type thermoelectric semiconductorpieces by removing all depthwise portions of the second integratedblock, other than the fitting parts.

This will result in a further considerable increase in the number ofthermocouples making up a thermoelectric device of a same size, and theoutput voltage of the thermoelectric device when used for generation ofpower can be additionally increased.

In the methods of fabricating the thermoelectric device described, theprocess of forming the grooved block of the n-type thermoelectricsemiconductor and grooved block of the p-type thermoelectricsemiconductor by applying a grooving process to an n-type thermoelectricsemiconductor block and p-type thermoelectric semiconductor block,respectively, such that a plurality of grooves are formed at a samepitch and in parallel with each other, leaving a depthwise portion ofthe respective blocks intact may be adopted for the grooved blockfabrication process described above.

Otherwise, a process of forming the grooved block of the n-typethermoelectric semiconductor and grooved block of the p-typethermoelectric semiconductor by molding n-type thermoelectricsemiconductor material and p-type thermoelectric semiconductor materialby use of a mold for the grooved block, respectively, and sintering thesame, may be adopted for the grooved block fabrication process describedabove.

In the methods of fabricating the thermoelectric device described, thethermoelectric device can be completed by applying a process of formingelectrodes for connecting the exposed n-type and p-type thermoelectricsemiconductor pieces to each other alternately and in series after thethermoelectric semiconductor pieces exposure process.

The method of fabricating the thermoelectric device may also comprise agrooving process applied to an n-type thermoelectric semiconductorcomposite block, prepared by bonding an n-type thermoelectricsemiconductor block to a base, and a p-type thermoelectric semiconductorcomposite block, prepared by bonding a p-type thermoelectricsemiconductor block to a base, for forming a plurality of grooves in then-type thermoelectric semiconductor block and the p-type thermoelectricsemiconductor block, respectively, at a same pitch, and to a depth closeto the interface between the respective thermoelectric semiconductorblocks and the base thereof; forming an n-type thermoelectricsemiconductor composite block and p-type thermoelectric semiconductorcomposite block, with the grooves formed therein, respectively; and, thefitting process, adhesion process, second grooving process,solidification process, and the like, applied to a pair ofthermoelectric semiconductor composite blocks, with the grooves formedtherein, forming an integrated block. Or by means of these processes,two integrated blocks may be formed, and fitted to each other after thesecond grooving process is applied thereto, forming a second integratedblock. Thereafter, the thermoelectric semiconductor pieces exposureprocess of exposing the n-type and p-type thermoelectric semiconductorpieces by removing the respective bases may be applied.

By adopting the processes described above, the thermoelectricsemiconductor material can be fully utilized without wastage.

It may be preferable to use bases having a surface area larger than anarea of the bonded surface of the respective thermoelectricsemiconductor blocks and to interpose spacers between portions of thebases of the n-type thermoelectric semiconductor composite block and thep-type thermoelectric semiconductor composite block, respectively, wherethe respective thermoelectric semiconductor blocks do not exist, and inthe fitting process, controlling a spacing between the bases to besubstantially equivalent to the thicknesses of the respectivethermoelectric semiconductor blocks.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 to 6 are perspective views of respective processes illustratinga first embodiment of a method of fabricating a thermoelectric deviceaccording to the invention;

FIGS. 7 and 8 are expanded views of the portion A of an integrated block3, shown by the imaginary lines in FIG. 3, illustrating variations ofthe adhesion process;

FIG. 9 is a plan view of a completed thermoelectric device according tothe first embodiment for explaining the construction of electrodes;

FIGS. 10 to 14 are perspective views of respective processesillustrating a second embodiment of a method of fabricating athermoelectric device according to the invention;

FIGS. 15 to 17 are perspective views showing the latter parts offabrication processes illustrating a third embodiment of a method offabricating a thermoelectric device according to the invention;

FIG. 18 is plan view of a completed thermoelectric device according tothe third embodiment for explaining the construction of electrodes;

FIGS. 19 to 21 are perspective views showing parts of fabricationprocesses illustrating a fourth embodiment of a method of fabricating athermoelectric device according to the invention;

FIGS. 22 to 24 are perspective views showing the first half offabrication processes illustrating a fifth embodiment of a method offabricating a thermoelectric device according to the invention;

FIGS. 25 to 26 are perspective views showing parts of fabricationprocesses illustrating a sixth embodiment of a method of fabricating athermoelectric device according to the invention;

FIGS. 27 to 29 are sectional views showing parts of fabricationprocesses illustrating a seventh embodiment of a method of fabricating athermoelectric device according to the invention;

FIGS. 30 and 31 are sectional views showing parts of fabricationprocesses illustrating an eighth embodiment of a method of fabricating athermoelectric device according to the invention;

FIGS. 32 and 33 are sectional views showing parts of fabricationprocesses illustrating a ninth embodiment of a method of fabricating athermoelectric device according to the invention; and

FIG. 34 is a sectional view showing an example of a mold used in forminga grooved block of thermoelectric semiconductor by means of injectionmolding.

BEST MODE FOR CARRYING OUT THE INVENTION

Embodiments of the method of fabricating a thermoelectric device incarrying out the invention in the best mode are described hereinafter.

First Embodiment: FIGS. 1 to 9

Firstly, a first embodiment of the method of fabricating athermoelectric device according to the invention is described withreference to FIGS. 1 to 9.

In the first embodiment of the invention, as shown in FIG. 1, an n-typethermoelectric semiconductor block 1 and a p-type thermoelectricsemiconductor block 2 are prepared. It is desirable that the both blocks1 and 2 be identical in all dimensions including the thickness thereof.For ease in identification of the respective blocks, all the surfaces ofthe n-type thermoelectric semiconductor block 1 are shown by thediagonally shaded areas. The same applies to all other figures shownhereinafter.

Subsequently, as shown in FIG. 2, a first grooving process offabricating a grooved block is applied, whereby a plurality oflongitudinal grooves 16 at a given pitch are formed parallel with eachother in the n-type thermoelectric semiconductor block 1 to a depth suchthat a thicknesswise portion 15 thereof is left intact, completing ann-type grooved block 11 provided with longitudinal partition walls 17formed thereon at a predetermined spacing. Similarly, a plurality oflongitudinal grooves 26 at a given pitch are formed parallel with eachother in the p-type thermoelectric semiconductor block 2 as well to adepth such that a thicknesswise portion 25 thereof is left intact,completing the p-type grooved block 21 provided with longitudinalpartition walls 27 formed thereon at a predetermined spacing.

In this instance, the longitudinal partition walls 17 of the n-typegrooved block 11 and the longitudinal partition walls 27 of the p-typegrooved block 21 are formed in a shape resembling the teeth of a comb,respectively, to enable the grooved blocks 11, 21 to snugly fit to eachother, and while the longitudinal grooves 16, 26 are formed at a samepitch, the width of the respective longitudinal grooves 16, 26 isrendered slightly wider than that of the respective longitudinalpartition walls 17, 27, to provide room for adhesion. Further, it isdesirable to equalize the depth of the respective longitudinal grooves16 to that of the respective longitudinal grooves 26.

The first grooving process of forming the longitudinal grooves 16, 26 isapplied to the n-type thermoelectric semiconductor block 1 and p-typethermoelectric semiconductor block 2, respectively, by, for example,polishing with the use of a wire saw, or by grinding with the use of adicing saw.

In the first embodiment of the invention, a BiTeSe sintered body is usedas the n-type thermoelectric semiconductor block 1 and a BiTeSb sinteredbody is used as the p-type thermoelectric semiconductor block 2, thedimensions of the both blocks being set at 12 mm×12 mm×4 mm. Thelongitudinal grooves 16, 26, each 70 μm wide, are formed at a pitch of120 μm in the grooved blocks 11 and 21, respectively, to a depth of 3 mmagainst 4 mm in the thickness of the respective grooved blocks.Accordingly, the width of the respective longitudinal partition walls17, 27 becomes 50 μm.

The method of fabricating the grooved blocks 11 and 21, composed ofthermoelectric semiconductors, is not limited to the method of finegrooving by machining as described above. The same may be fabricated bya molding method such as an injection molding method, or the like, anexample of which will be described later.

Subsequently, as shown in FIG. 3, a fitting process and adhesion processare applied, whereby the n-type grooved block 11 and p-type groovedblock 21 are fitted to each other such that the longitudinal partitionwalls 27, 17 of the respective blocks are inserted into the longitudinalgrooves 16, 26 of the respective opposite blocks, and both blocks arefitted to each other by filling up gaps in fitting parts therebetweenwith an adhesive insulating material, forming an integrated block 3.

In these processes of forming the integrated block 3, wherein the n-typegrooved block 11 and p-type grooved block 21 are fitted to each other,and adhered together with the insulating material, adhesive layersformed thereby need to have the function of ensuring electricalinsulation between the n-type grooved block 11 and p-type grooved block21 besides the function of bonding the two blocks together.

For example, in the case where the inner walls of the longitudinalgrooves 16, 26 are finished to have very smooth surfaces by polishingwith the use of a wire saw, such electrical insulation can be ensured bysimply immersing portions of the integrated block 3 in an adhesive ofhigh fluidity prior to the adhesion process such that gaps between thelongitudinal grooves 16, 26 and the longitudinal partition walls 27, 17,respectively, are filled up with the adhesive due to the capillaryeffect.

On the other hand, in the case where the inner walls of the longitudinalgrooves 16, 26 are finished up into somewhat rough surfaces, maintenanceof electrical insulation is ensured by applying a method as illustratedin FIG. 7 or 8 showing an enlarged view of the part A of the integratedblock 3, as indicated by the imaginary lines in FIG. 3.

In the method shown in FIG. 7, an insulation film 31 is formed on thesurfaces of both the longitudinal partition walls 17 and thelongitudinal grooves 16 of the n-type grooved block 11, and the p-typegrooved block 21 is fitted onto the insulation film 31 so that gapsbetween the insulation film 31 and the longitudinal partition walls 27as well as the longitudinal grooves 26 thereof are filled up with theadhesive taking advantage of the capillary effect as described in theforegoing, forming an adhesive layer 32 after the adhesive is cured. Theintegrated block 3 is thus completed.

For the insulation film 31, either an inorganic film composed of siliconoxide, aluminum oxide, silicon nitride or the like, or an organic filmcomposed of polyimide or the like may be used.

The insulation film 31 may be alternatively formed on the surfaces ofthe longitudinal partition walls 27 as well as the longitudinal grooves26 of the p-type grooved block 21. Further, electrical insulation isadditionally ensured by forming the insulation film 31 on the surfacesof both the n-type grooved block 11 and p-type grooved block 21, to befitted with each other.

In the method shown in FIG. 8, the integrated block 3 is fabricated byuse of an adhesive with insulating spacers 33 dispersed therein. Forexample, 5 wt % of glass beads spherical in shape, 8 μm in average grainsize, are added as the insulating spacers 33 to an epoxy adhesive. Thiswill cause the glass beads to be dispersed substantially evenly in theadhesive layer 32 such that the n-type grooved block 11 and p-typegrooved block 21 are forced to be isolated spatially from each other bythe insulating spacers 33 composed of the glass beads, ensuringelectrical insulation therebetween.

As shown in FIG. 4, a second grooving process is applied to theintegrated block 3 shown in FIG. 3, completed by applying the fittingprocess and adhesion process as described hereinbefore, thereby formingtransverse grooves 46. The block shown in FIG. 4, completed by formingthe transverse grooves 46 in the integrated block 3, is referred to as agrooved integrated block 4 hereinafter.

In the process of forming the transverse grooves 46, a plurality of thetransverse grooves 46 are formed at a given pitch in the directioncrossing the direction in which the longitudinal grooves have beenformed in the first grooving process as described in FIG. 3, leaving athicknesswise portion 45 of the grooved integrated block 4 intact sothat transverse partition walls 47 are formed at a predeterminedspacing. In this process, the transverse grooves 46 may be formed so asto cross the longitudinal grooves 16, 26 formed in the first groovingprocess at optional angles. However, they most preferably cross at rightangles as shown in FIG. 4.

Further, in this embodiment, the transverse grooves 46 are formed in theintegrated block 3 from the side of the p-type grooved block 21 as shownin FIG. 4. However, the same may be formed therein conversely from theside of the n-type grooved block 11. Otherwise, the same may be formedin the fitting parts from the front face side or from the rear face sideof the integrated block 3 shown in FIG. 3.

The transverse grooves 46 are preferably formed in the integrated block3 to a depth such that the fitting parts between the n-type groovedblock 11 and the p-type grooved block 21 are severed thereby.

As opposed to the case of the longitudinal grooves 16, 26, it ispreferable that the width of the respective transverse grooves 46 berendered as narrow as possible. This is because it is the transversepartition walls 47 that contribute to the capacity of power generationof the thermoelectric device as is shown from subsequent steps ofprocessing, and consequently, from the viewpoint of performance of thethermoelectric device, the regions for the transverse grooves 46 shouldbe reduced in size as much as possible.

Accordingly, in the first embodiment of the invention, the transversegrooves 46, 40 μm in width and 4 mm in depth, are formed at a pitch of120 μm. Incidentally, the width 40 μm of the respective transversegrooves 46 represents a substantial limit size for the width of a grooveformed by processing with the use of a wire saw.

Subsequently to the foregoing step of processing, a solidificationprocess as shown in FIG. 5 is applied. That is, the respectivetransverse grooves 46 of the grooved integrated block 4 shown in FIG. 4are filled up with insulating resin (insulation member), forminginsulating resin layers 54 after the insulation member is cured. A blocksolidified with the insulating resin layers 54 is referred to as agrooved integrated block 4′ hereinafter.

Thereafter, a process of exposing thermoelectric semiconductor pieces isapplied to the grooved integrated block 4′ solidified with theinsulating resin layers 54, whereby portions (portions having thicknessdenoted by a, b, respectively, in FIG. 5) of the grooved integratedblock 4′ which have been left intact without the grooving processapplied thereto during the first and second grooving processes describedin the foregoing are removed by polishing, or grinding the upper andunder surfaces of the grooved integrated block 4′, and the remainder isfinished up such that only the fitting parts shown in FIG. 3, whereinthe longitudinal grooves 16, 26, composed of the n-type thermoelectricsemiconductor, and p-type thermoelectric semiconductor, respectively,are fitted to the longitudinal partition walls 27, 17, composed of thep-type thermoelectric semiconductor, and n-type thermoelectricsemiconductor, respectively, and a portion wherein the transversegrooves 46 are formed, is left intact. A thermoelectric device block 5shown in FIG. 6 is thus obtained.

In the thermoelectric device block 5, a multitude of n-typethermoelectric semiconductor pieces 51, and p-type thermoelectricsemiconductor pieces 52 are insulated from each other via the insulatingresin layers 54, and integrally adhered to each other while the upper aswell as under surfaces thereof are exposed.

In the final step of processing, a process of forming electrodes isapplied to both the upper and under surfaces of the thermoelectricdevice block 5 shown in FIG. 6 such that the n-type thermoelectricsemiconductor pieces 51 and p-type thermoelectric semiconductor pieces52 are connected with each other, alternately and electrically inseries, thereby obtaining a thermoelectric device 6 shown in FIG. 9.

FIG. 9 is a plan view of the thermoelectric device 6, as seen fromdirectly above, illustrating various electrodes formed on the upper aswell as under surfaces thereof.

In the figure, upper surface electrodes 61 a circular in shape asindicated by the solid lines and under surface electrodes 62 a circularin shape as indicated by the broken lines are electrodes for connectingtogether the n-type thermoelectric semiconductor pieces 51 and p-typethermoelectric semiconductor pieces 52 adjacent to each other,electrically in series, forming a multitude of thermocouples. Uppersurface electrodes 61 b and under surface electrodes 62 b, resemblingthe letter L in shape, are electrodes required in the periphery regionof the thermoelectric device 6 for connecting the n-type or p-typethermoelectric semiconductor pieces in parallel although it is deemedunusable. The respective thermoelectric semiconductor pieces 51, 52 areinsulated from each other by means of the adhesive layers 32 and theinsulating resin layers 54. Further, under surface electrodes 63, 64, inthe shape of a small circle indicated by the broken lines are electrodesfor outputting voltage externally.

Each of the electrodes described above is formed by depositing a gold(Au) film on both the upper and under surfaces of the thermoelectricdevice block 5 shown in FIG. 6 by means of the vacuum coating method,sputtering method, electroless plating method, or the like, and then, bypatterning on the gold film by the photolithographic technique andetching technique.

In the case where the upper and under surfaces of the thermoelectricdevice block 5, on which the electrodes are to be formed, are likely tocause a problem of surface roughness when finished by only grinding asdescribed hereinbefore, it is desirable to render the surfaces smootherby lapping, or the like as this will prevent occurrence of faults withthe electrodes (such as breakage) thereof.

For the electrodes, use can be made of not only the gold film but alsoother metal film, for example, a Cu film, Al film, Ni film, Fe film, ora multi-layer film (for example, Al/Ni film) composed of the aforesaidfilms combined together. Further, in forming the electrodes, use may bemade of the printing method, masked vapor deposition method, or a methodwhereby the electrodes are patterned beforehand on an insulatingsheet-like material made of glass or ceramic, and the sheet-likematerial as a whole is pasted on the surfaces.

In the method according to the first embodiment of the invention, thelongitudinal partition walls 17, 27 and the transverse partition walls47, composed of the thermoelectric semiconductor materials, and verythin, are formed in the first and second grooving processes as shown inFIGS. 2 and 4. Although these partition walls, individually, are verythin and fragile, the same together constitute an integrated block, andprocessing operations can be performed on respective blocks as a wholewithout need of performing delicate operations such as holdingindividual partition walls for transfer and stacking the same, and thelike. Hence, in comparison with the conventional method disclosed inJapanese Patent Laid-open Publication No. 63-20880, it is possible tofabricate a thermoelectric device incorporating a multitude of smallsized thermocouples efficiently with ease, overcoming the problem offragility.

In the case of another conventional method disclosed in Japanese PatentLaid-open Publication No. 8-43555, integrated blocks are used. However,thermoelectric semiconductors are bonded to separate base members, andprocessed so as to form a multitude of columnar shapes. As a result,extreme difficulties are still encountered in fabrication of a productdue to the serious problem of fragility. As opposed to such a method,the method according to the first embodiment of the invention is amethod of fabrication whereby thermoelectric semiconductors are alwaysprocessed when the same are in the form of an integrated block, thusenabling fine structural processing and assembling of thermoelectricsemiconductor material, which is a very fragile material, to be carriedout with ease. Consequently, it is possible to efficiently fabricatewith ease a thermoelectric device provided with a multitude ofthermocouples in order to enhance the output voltage.

However, the process of exposing thermoelectric semiconductor pieces maybe applied straight to the integrated block 3 shown in FIG. 3 byomitting the second grooving process, and the solidification processwhereby grooved parts (the transverse grooves 47 in FIG. 4) are filledup with the insulation member, which is then solidified, forming theinsulating resin layers 54 shown in FIG. 5, as applied in carrying outthe first embodiment. Such omission, however, will result in a decreasein the number of thermocouples making up the thermoelectric device.

In this case, the grinding process, and the like are applied to theupper as well as under surfaces of the integrated block 3 fabricated bymeans of the fitting process and adhesion process as shown in FIG. 3,and by removing portions of the integrated block 3, other than partswhere the longitudinal partition walls 17, 27 of the n-type groovedblock 11 and p-type grooved block 21, respectively, are fitted to thelongitudinal grooves 16, 26, the thermoelectric device block with then-type and p-type thermoelectric semiconductor pieces exposed can befabricated.

Thereafter, the process of forming the electrodes is applied thereto,whereby electrodes for connecting the exposed n-type and p-typethermoelectric semiconductor pieces (that is, the longitudinal partitionwalls 17 of the n-type groove block 11 and the longitudinal partitionwalls 27 of the p-type groove block 21) alternately to each other and inseries are formed on the upper as well as under surfaces of thethermoelectric device block, thus fabricating the thermoelectric device.

Second Embodiment: FIGS. 10 to 14

Next, a second embodiment of the method of fabricating a thermoelectricdevice according to the invention is described hereinafter withreference to FIGS. 10 to 14. In these figures, parts corresponding tothose previously described with reference to the first embodiment shownin FIGS. 1 to 5 are denoted by the same reference numerals.

In the second embodiment, as shown in FIG. 10, an n-type thermoelectricsemiconductor composite block 12 formed by bonding an n-typethermoelectric semiconductor block 1 to a base 10, and a p-typethermoelectric semiconductor composite block 22 formed by bonding ap-type thermoelectric semiconductor block 2 to a base 20 are firstprepared. It is desirable that the n-type thermoelectric semiconductorblock 1 and the p-type thermoelectric semiconductor block 2 be identicalin all dimensions including the thickness thereof.

The thermoelectric semiconductor blocks 1, 2 are bonded to the bases 10,20, respectively, with an adhesive or wax. Further, for the bases 10,20, use can be made of various materials having a given hardness such asglass, ceramic, plastic, metal, and the like.

Subsequently, a grooving process, the same as applied in the firstgrooving process in the first embodiment is applied to the respectivethermoelectric semiconductor blocks 1, 2 of the thermoelectricsemiconductor composite blocks 12, 22, respectively, and as shown inFIG. 11, longitudinal grooves 16, 26 as well as longitudinal partitionwalls 17, 27, resembling the teeth of a comb in shape, are formed,fabricating an n-type grooved composite block 13 and a p-type groovedcomposite block 23. The pitch and width of the longitudinal grooves 16,26 are the same as in the case of the first embodiment, however, thedepth thereof is set to be substantially close to the interface betweenthe thermoelectric semiconductor block 1, or 2 and the base 10 or 20,respectively. More specifically, the depth is selected from amongslightly short of the interface, down to just the interface, or belowthe interface, cutting slightly into the base 10 or 20, depending on thecircumstance.

Thereafter, a fitting process whereby the n-type grooved composite block13 and p-type grooved composite block 23 are fitted to each other suchthat respective grooved surfaces face each other is applied, and then,an adhesion process whereby gaps in fitting parts between the n-typegrooved composite block 13 and p-type grooved composite block 23 whichare fitted to each other are filled up with an adhesive insulationmember so that the n-type grooved composite block 13 and p-type groovedcomposite block 23 are adhered to each other is applied, therebyfabricating an integrated block 3′ shown in FIG. 12.

Subsequently, a grooving process, the same as applied in the secondgrooving process in the first embodiment, as shown in FIG. 4, is appliedto the integrated block 3′ as shown in FIG. 13, whereby transversegrooves 46 and transverse partition walls 47 are formed, fabricating agrooved integrated block 14. In this instance, the transverse grooves 46are cut into one of the grooved composite blocks to a depth close to theinterface thereof with the base 10 or 20 of the other grooved compositeblock and in such a direction as to cross (at right angles, in thisembodiment) the longitudinal grooves 16, 26, and the longitudinalpartition walls 17, 27, formed in the first grooving process.

Then, as shown in FIG. 14, a solidification process is applied wherebygrooved parts, that is, the transverse grooves 46, are filled up withinsulating resin (insulation member), and the insulating resin is thensolidified, forming insulating resin layers 54. A block solidified withthe insulating resin layers 54 is referred to hereafter as a groovedintegrated block 14′.

Thereafter, a process of exposing thermoelectric semiconductor pieces isapplied to the grooved integrated block 14′ shown in FIG. 14, wherebythe bases 10 and 20, that is, bottom and top portions of the groovedintegrated block 14′, are removed, obtaining a thermoelectric deviceblock 5, the same as shown in FIG. 6 in the case of the firstembodiment. The base on the side where the grooving process is applied(the base 20 in the example shown in FIG. 13) may be removed prior toforming the transverse grooves 46.

Further, by applying a process of forming electrodes for forming theelectrodes on the upper and under surfaces of the thermoelectric deviceblock 5 such that n-type thermoelectric semiconductor pieces 51 andp-type thermoelectric semiconductor pieces 52 are connected to eachother alternately and electrically in series, a thermoelectric device 6,the same as shown in FIG. 9, can be fabricated.

In the method according to the second embodiment, the bases 10, 20 areemployed to integrally support the longitudinal partition walls 17, 27,and the transverse partition walls 47 in place of portions left intactwithout the grooving process applied thereto (the portions 15, 25 shownin FIG. 2) of the thermoelectric semiconductor blocks 1 and 2,respectively, which will be eventually removed by grinding as in theaforesaid first embodiment. Consequently, effective use can be made ofportions of the thermoelectric semiconductor material, in regions closeto the upper and under surfaces thereof, reducing unusable portionsthereof. Therefore, the method has an advantage of remarkably improvingthe utilization efficiency of the material.

Other merits of operation according to this embodiment are the same asfor the first embodiment.

Third Embodiment: FIGS. 15 to 18

Now, a third embodiment of the method of fabricating a thermoelectricdevice according to the invention is described hereinafter withreference to FIGS. 15 to 18. The first half of a process applied incarrying out the third embodiment is the same as for the firstembodiment described with reference to FIGS. 1 to 3, and accordingly,will only be briefly described referring to these figures.

In the third embodiment, two each of the n-type thermoelectricsemiconductor blocks 1 and p-type thermoelectric semiconductor blocks 2as shown in FIG. 1 are prepared. Subsequently, a first grooving processas shown in FIG. 2 is applied to the respective thermoelectricsemiconductor blocks, whereby a plurality of longitudinal grooves 16,26, and longitudinal partition walls 17, 27 are formed at a same pitch,and parallel with each other such that the depth of the former is equalto the height of the latter, fabricating two pairs of n-type groovedblocks 11, and p-type grooved blocks 21.

In this case as well, the two pairs of the n-type grooved blocks 11, andp-type grooved blocks 21 may be fabricated by a process of fabricatinggrooved blocks using a molding method, which will be described later.

Subsequently, by applying a fitting process as shown in FIG. 3, wherebythe respective n-type grooved blocks 11 and p-type grooved blocks 21 arefitted to each other, and a first adhesion process of forming integratedblocks, whereby the grooved blocks fitted are adhered to each other byfilling up gaps in fitting parts thereof with an adhesive insulatingmaterial, two integrated blocks 3 are fabricated.

Thereafter, a second grooving process is applied to one of the twointegrated blocks 3 from the side of the p-type grooved block 21 shownin FIG. 3, and to the other from the side of the n-type grooved block11, whereby a plurality of grooves parallel with each other are formedat a same pitch in the direction crossing the direction in which thefirst grooving process has been applied, (at right angles, in thisembodiment), fabricating a pair of grooved integrated blocks 43A, 43B,wherein a plurality of transverse grooves 46 and transverse partitionwalls 47 are formed as shown in FIG. 15, the depth of the former beingequal to the height of the latter.

In this case, the dimensions of the transverse grooves 46 and transversepartition walls 47 are rendered similar to those of the longitudinalgrooves 16, 26, and longitudinal partition walls 17, 27, described inthe first embodiment with reference to FIG. 2, so that the transversegrooves 46 in one of the grooved integrated blocks, and the transversepartition walls 47 in the other of the grooved integrated blocks can befitted to each other. That is, in the grooved integrated blocks 43A,43B, shown in FIG. 15, the transverse grooves 46 are formed at a samepitch, and the width of the respective transverse grooves 46 is renderedwider than that of the respective transverse partition walls 47.

Subsequently, as shown in FIG. 16, by applying a second fitting processwhereby the pair of grooved integrated blocks 43A, 43B are combined witheach other by fitting the respective transverse partition walls 47 intothe respective transverse grooves 46, and further, by applying a secondadhesion process whereby the grooved integrated blocks fitted togetherare integrally adhered to each other by filling up gaps between fittingparts with an adhesive insulating material, the pair of the groovedintegrated blocks are integrally joined together, forming a doublyintegrated block 44.

Further, for fitting and adhering together the grooved integrated blocks43A with 43B, the methods previously described in the first embodimentwith reference to FIGS. 3, 7, and 8 are applied.

Thereafter, a process of exposing thermoelectric semiconductor pieces isapplied to the doubly integrated block 44. That is, portions of thedoubly integrated block 44, other than a depthwise portion denoted by din FIG. 16, are removed by polishing or grinding the upper as well asunder surfaces thereof so that the remainder is finished up, leavingintact regions where the longitudinal grooves 16, 26, the transversegrooves 46, the longitudinal partition walls 27, 17, and the transversepartition walls 47, composed of either of the n-type thermoelectricsemiconductor and p-type thermoelectric semiconductor, are all fitted toeach other. Thus, as shown in FIG. 17, a thermoelectric device block 50wherein n-type thermoelectric semiconductor pieces 51 and p-typethermoelectric semiconductor pieces 52 are alternately arranged isfabricated.

In integrally joining the grooved integrated blocks 43A with 43B incarrying out this embodiment, preferable fabrication conditions requirethat the n-type thermoelectric semiconductor pieces 51 and p-typethermoelectric semiconductor pieces 52 be arranged regularly like acheckerboard as shown in FIG. 17. Accordingly, respective positionsthereof need to be aligned, which may be accomplished by providing abenchmark face on the periphery of each of the grooved integratedblocks, and joining the same together based on the benchmark face usinga jig.

Such alignment in positioning will facilitate wiring work in a processof electrode wiring described hereinafter because of standardized andsimplified shapes and layout of the electrodes as shown in FIG. 18.Furthermore, this will contribute to improvement in the utilizationefficiency of the thermoelectric semiconductors because thethermoelectric semiconductor pieces located in the edge portions on theopposite sides in FIG. 9, not contributing to electrical connection inseries, can be eliminated in this way.

Then, a process of forming electrodes is applied to the upper as well asunder surfaces of the thermoelectric device block 50 such that then-type thermoelectric semiconductor pieces 51 and p-type thermoelectricsemiconductor pieces 52 are alternately and electrically connected witheach other in series, thereby fabricating a thermoelectric device 60shown in FIG. 18.

FIG. 18 is a plan view of the thermoelectric device 60, as seen directlyfrom above, and respective electrodes are formed on both the uppersurface and the under surface thereof.

Upper surface electrodes 61 circular in shape as indicated by the solidlines, formed on the upper surface of the thermoelectric device block 50and under surface electrodes 62 circular in shape as indicated by thebroken lines, formed on the under surface thereof are electrodes forconnecting together the n-type thermoelectric semiconductor pieces 51and p-type thermoelectric semiconductor pieces 52, adjacent to eachother, in series, forming a plurality of thermocouples. Further, undersurface electrodes 63, 64 are electrodes for outputting voltageexternally.

Each of the electrodes denoted by 61 to 64 is formed by depositing agold (Au) film on both the upper and under surfaces of thethermoelectric device block 50 shown in FIG. 17 by means of the vacuumcoating method, sputtering method, electroless plating method, or thelike, and then, by patterning on the gold film by use of thephotolithographic technique and etching technique. Further, as amaterial for the electrodes, use can be made of not only gold film butalso various other materials cited in the first embodiment described inthe foregoing.

In the case where surface roughness of the upper and under surfaces ofthe thermoelectric device block 50, on which the electrodes 61 to 64 areformed, is likely to cause a problem as with the case of the firstembodiment, it is desirable to render the surfaces smoother by lapping,or the like, as occurrence of faults with the electrodes (such asbreakage) thereof is inhibited in this way.

Accordingly, the method according to the third embodiment of theinvention has an advantage in that the upper surface electrodes 61 b andunder surface electrodes 62 b formed in the shape resembling the letterL as shown in FIG. 9, which are required in the first and secondembodiments, can be dispensed with, facilitating the wiring process andenabling effective use of the thermoelectric semiconductor material.

Further, with the thermoelectric device according to the thirdembodiment, the number of thermoelectric semiconductor piecesincorporated therein per unit volume thereof can be substantiallydoubled over that in the case of the first embodiment or the secondembodiment so that a thermoelectric device smaller in size, but capableof outputting a higher voltage, will be obtained.

With the method according to the third embodiment, the side of theintegrated block 3 shown in FIG. 3, on which the grooving process isapplied, may be ground beforehand prior to forming the transversegrooves 46 as shown in FIG. 15 such that fitting parts between thelongitudinal grooves 16, 26, and the longitudinal partition walls 17,27, composed of the n-type thermoelectric semiconductor and p-typethermoelectric semiconductor, respectively, are exposed.

If the transverse grooves 46 are formed subsequently, all of thelongitudinal grooves 16, 26, the transverse grooves 46, the longitudinalpartition walls 17, 27, and the transverse partition walls 47, composedof the n-type thermoelectric semiconductor, and p-type thermoelectricsemiconductor, respectively, are fitted together in their entirety whenthe second fitting process shown in FIG. 16 is applied. As a result, inthe process of exposing the thermoelectric semiconductor pieces, thethermoelectric semiconductor pieces can be formed by leaving intact aportion of thermoelectric semiconductor material, corresponding to thefull height of the longitudinal partition walls 17, 27 with the resultthat the utilization efficiency of the thermoelectric semiconductormaterial is enhanced.

Fourth Embodiment: FIGS. 19 to 21

A fourth embodiment of a method of fabricating a thermoelectric deviceaccording to the invention is described hereinafter with reference toFIGS. 19 to 21. The first half of a process applied in carrying out thefourth embodiment is the same as for the second embodiment describedwith reference to FIGS. 10 to 12, and accordingly, will only be brieflydescribed referring to these figures.

In the fourth embodiment, two each of n-type thermoelectricsemiconductor composite blocks 12 formed by bonding the n-typethermoelectric semiconductor block 1 to the base 10, shown in FIG. 10,and p-type thermoelectric semiconductor composite blocks 22 formed bybonding the p-type thermoelectric semiconductor block 2 to the base 20,shown in FIG. 10, are prepared.

Then, a first grooving process is applied to the respectivethermoelectric semiconductor composite blocks 12, 22, whereby aplurality of grooves at a same pitch are formed in the n-typethermoelectric semiconductor block 1, and the p-type thermoelectricsemiconductor block 2, respectively, to a depth close to the interfacebetween the thermoelectric semiconductor block 1, or 2 and the base 10or 20 as shown in FIG. 11 such that longitudinal grooves 16, 26 as wellas longitudinal partition walls 17, 27 are formed in a shape resemblingthe teeth of a comb. Thus, two pairs of n-type grooved composite blocks13 and p-type grooved composite blocks 23 are fabricated. The positionsof the respective longitudinal grooves 16 of the n-type groovedcomposite block 13 are preferably deviated from those of thecorresponding longitudinal grooves 26 of the p-type grooved compositeblock 23 by a half of the pitch.

Subsequently, a first fitting process is applied to the two pairs of then-type thermoelectric semiconductor composite blocks 13 and p-typethermoelectric semiconductor composite blocks 23, to which the groovingprocess described above has been applied, respectively, wherebyrespective grooved n-type thermoelectric semiconductor composite blocks13 and respective grooved p-type thermoelectric semiconductor compositeblocks 23 are fitted to each other such that grooved surfaces of eachpair face each other, and then a first adhesion process is applied tothe two pairs of the grooved n-type thermoelectric semiconductorcomposite blocks 13 and grooved p-type thermoelectric semiconductorcomposite blocks 23, fitted to each other through the first fittingprocess, whereby both blocks in each pair are adhered to each other byfilling up gaps in fitting parts therebetween with an adhesiveinsulation member, thereby fabricating two integrated blocks 3′ as shownin FIG. 12.

With one of the two integrated blocks 3′, the base 20 on the side of thep-type thermoelectric semiconductor block is removed while with theother, the base 10 on the side of the n-type thermoelectricsemiconductor block is removed, obtaining a pair of integrated blocks142A, 142B, with the longitudinal partition walls 17 of the n-typethermoelectric semiconductor and the longitudinal partition walls 27 ofthe p-type thermoelectric semiconductor, exposed on either the uppersurface or under surface thereof, respectively, as shown in FIG. 19.

Subsequently, a process, the same as the second grooving processdescribed in the second embodiment described hereinbefore with referenceto FIG. 13, is applied to the pair of the integrated blocks 142A, 142B,from the side where the base 10 or the base 20 is removed, whereby aplurality of grooves at a same pitch are formed in the directioncrossing the direction in which the first grooving process has beenapplied (at right angles, in this embodiment) to a depth close to theinterface between the respective thermoelectric semiconductor blocks andthe base 20 or the base 10 which has not been removed, therebyfabricating two grooved integrated blocks 143A, 143B, with a pluralityof transverse grooves 46 and transverse partition walls 47 formedtherein. In this connection, it is preferable that the transversegrooves 46 in one of the grooved integrated blocks, e.g. 143A, areformed such that the positions thereof are deviated by a half of thepitch from those of the transverse grooves 46 formed in the other of thegrooved integrated blocks, e.g. 143B.

Subsequently, by applying a second fitting process whereby the twogrooved integrated blocks 143A, 143B are fitted to each other such thatrespective grooved surfaces face each other, and then a second adhesionprocess, whereby the two grooved integrated blocks 143A, 143B, thusfitted to each other, are adhered together by filling up gaps in fittingparts therebetween with an adhesive insulation member, a doublyintegrated block 144 shown in FIG. 21 is fabricated.

In this case, similarly to the case of the third embodiment, therelative position of the n-type thermoelectric semiconductor pieces 51and p-type thermoelectric semiconductor pieces 52 need to be controlledso as to be arranged like a checkerboard as shown in FIG. 17 whenfitting the two grooved integrated blocks 143A, 143B to each other.

As described in the third embodiment, alignment of respective positionscan be accomplished by providing a benchmark face on the periphery ofeach of the grooved integrated blocks. Further, in the fourthembodiment, precision alignment of the respective positions may beattained through direct observation of the respective n-typethermoelectric semiconductor pieces 51 and respective p-typethermoelectric semiconductor pieces 52 by use of a microscope if atransparent member such as glass, or the like is used for the bases 10and 20.

Then, by removing the bases 10 and 20 from the doubly integrated block144, a thermoelectric device block, the same as the thermoelectricdevice block 50 shown in FIG. 17 with reference to the third embodiment,is obtained. Subsequently, by providing electrodes as same as theelectrodes 61 to 64 illustrated in FIG. 18, a thermoelectric device, thesame as the thermoelectric device 60 shown in FIG. 18, is fabricated.

In this embodiment, before the second grooving process is applied to thetwo integrated blocks 3′, the base 20 or 10 on the side where theprocess of forming the transverse grooves 46 are applied is removed fromthe respective integrated blocks 3′ so that when the pair of the groovedintegrated blocks 143A and 143B, with the transverse grooves 46 formedtherein, are fitted to each other, the thermoelectric semiconductors asa whole can be fitted to each other, enabling all thermoelectricsemiconductors left intact to be put to use for the thermoelectricsemiconductor pieces without any wastage thereof.

However, since such a step of processing is not essential, the base 10or the base 20 may be removed after the second grooving process(formation of the transverse grooves) has been applied instead of firstremoving the base 10 or the base 20.

Fifth Embodiment: FIGS. 22 to 24

A fifth embodiment of a method of fabricating a thermoelectric deviceaccording to the invention is described hereinafter with reference toFIGS. 22 to 24.

In the method according to the fifth embodiment, an n-typethermoelectric semiconductor block 1 and a p-type thermoelectricsemiconductor block 2 are bonded, respectively, to each of two largebases 110, 120 (hereinafter referred to as large bases), similarly tothe case of the second embodiment, fabricating a pair of an n-typethermoelectric semiconductor composite block 91 and p-typethermoelectric semiconductor composite block 92.

More specifically, the large bases 110, 120 employed in carrying outthis embodiment have a surface area larger than a bonded surface area ofthe respective thermoelectric semiconductor blocks 1, 2.

Similarly to the case of the second embodiment, longitudinal grooves 16,26, and longitudinal partition walls 17, 27 are formed in thethermoelectric semiconductor blocks 1 and 2, respectively, by applying afirst grooving process thereto, fabricating an n-type grooved compositeblock 181, and p-type grooved composite block 182 shown in FIG. 23. Inthis instance, the longitudinal grooves 16, 26 are preferably formed toa depth cutting into a portion of the large bases 110, 120,respectively. The reason for this is to make the most of the effect ofspacers 190 in a fitting process described hereinafter with reference toFIG. 24 such that n-type as well as p-type thermoelectric semiconductorscan be put to use efficiently.

Then, as shown in FIG. 24, a first fitting process is applied, wherebythe n-type grooved composite block 181 and p-type grooved compositeblock 182, shown in FIG. 23, are combined to be fitted to each other. Inthis instance, by interposing the spacers 190 between the large bases110 and 120, a spacing D between the two large bases 110 and 120 iscontrolled (restrained) accurately to match the height of thelongitudinal partition walls 17, 27, composed of a thermoelectricsemiconductor, corresponding to the thickness of the respectivethermoelectric semiconductor blocks 1, 2.

For example, by equalizing the thickness of the n-type thermoelectricsemiconductor block 1, p-type thermoelectric semiconductor block 2, andspacers 190, respectively, the spacing D between the two large bases 110and 120 can be maintained at a given distance, enabling the longitudinalpartition walls 17, 27, composed of the n-type and p-type thermoelectricsemiconductors, respectively, to be arranged without unevenness inthickness.

That is, even in case there is no uniformity in the depth of thelongitudinal grooves 16, 26, respectively, the n-type and p-typethermoelectric semiconductors can be arranged so as to have nounevenness in thickness with respect to each other by use of the spacers190 with the result that wasteful polishing or grinding of the n-typeand p-type thermoelectric semiconductors can be avoided, enablingimprovement in utilization efficiency thereof.

After the first fitting process with the use of the spacers 190, then-type grooved composite block 181 and p-type grooved composite block182 are adhered to each other by filling up gaps in fitting partstherebetween with an adhesive insulation member, obtaining an integratedcomposite block 193 shown in FIG. 24.

Subsequently, a second grooving process is applied, fabricating agrooved integrated composite block with transverse grooves andtransverse partition walls formed therein, similar to the groovedintegrated block 14 shown in FIG. 13 with reference to the secondembodiment, and insulating resin layers, the same as the insulatingresin layers 54 shown in FIG. 14, are formed by filling up therespective transverse grooves with insulating resin, and by curing theinsulating resin. Thereafter, by removing the large bases 110, 120, athermoelectric device block, the same as the thermoelectric device blockshown in FIG. 6, is obtained. Further, as shown in FIG. 9, by formingvarious electrodes on the upper as well as under surfaces of thethermoelectric device block, and connecting the respectivethermoelectric semiconductor pieces with each other, alternately and inseries, the thermoelectric device 6 can be fabricated.

Sixth Embodiment: FIGS. 25 and 26

Next, a sixth embodiment of the method of fabricating a thermoelectricdevice according to the invention using the integrated composite blocksdescribed in carrying out the fifth embodiment is described hereinafterwith reference to FIGS. 25 and 26.

In the method according to the sixth embodiment, two integratedcomposite blocks 193 are fabricated by means of processes, the same asthe respective processes described in the fifth embodiment withreference to FIGS. 22 to 24.

Subsequently, a second grooving process (formation of transversegrooves) is applied to the two integrated composite blocks 193,respectively, whereby a large base 110 or 120, on the side where thesecond grooving process is applied, is removed in a manner similar tothe process as applied in the fourth embodiment described with referenceto FIG. 19, fabricating a pair of grooved integrated composite blocks203A, 203B as shown in FIG. 25, provided with a plurality of transversegrooves 46 as well as transverse partition walls 47 formed therein,respectively, so as to be fitted to each other.

Thereafter, the pair of grooved integrated composite blocks 203A and203B are fitted to each other while maintaining a spacing between thelarge bases 110 and 120 at a given distance (a value equivalent to theheight of the thermoelectric semiconductors left intact) with the use ofspacers 190, and gaps in fitting parts therebetween are filled up withan adhesive insulation member, fabricating a doubly integrated block213, as shown in FIG. 26.

Then, n-type and p-type thermoelectric semiconductor pieces 51, and 52are exposed by removing the large bases 110, and 120 of the doublyintegrated block 213, thereby obtaining a thermoelectric device block,the same as the thermoelectric device block shown in FIG. 17 withreference to the third embodiment.

Further, by forming electrodes 81 to 84 on the upper as well as undersurfaces of the thermoelectric device block as shown in FIG. 18, andconnecting respective thermoelectric semiconductor pieces 51, 52 witheach other, alternately and in series, the thermoelectric device 60 canbe fabricated.

Provided that the thermoelectric device 60 fabricated in the third,fourth, or sixth embodiment has dimensions of 10 mm×10 mm×2 mm afterremoving the peripheral region of the thermoelectric device block, 12 mmsquare, about 3400 couples of thermocouples can be integrated therein.

When a temperature difference of 1.50° C. was applied to thethermoelectric device 60, an output voltage at 2.0 V was obtained.

Thus, as the thermoelectric device 60 is small enough to be encased in asmall portable electronic device such as a wrist watch and yet has anopen circuit output voltage at a level high enough to drive a wristwatch, it is possible to drive various portable electronic devices withthe thermoelectric device 60 in combination with a booster circuit.

Seventh Embodiment: FIGS. 27 to 29

Next, a seventh embodiment of the method of fabricating a thermoelectricdevice according to the invention is described hereinafter withreference to FIGS. 27 to 29.

In the method according to the seventh embodiment of the invention, ann-type thermoelectric semiconductor block 1 and a p-type thermoelectricsemiconductor block 2 as shown in FIG. 1 with reference to the firstembodiment are first prepared, and as shown in FIG. 27, a metal coatedlayer 223 is formed on the surfaces of the respective thermoelectricsemiconductor blocks 1, 2, that is, at least the surface bonded to abase, and the surface on the opposite side thereof (the surface on whichelectrodes are formed in a process of forming electrodes applied lateron) by means of plating, vapor deposition, sputtering, or the like.Thus, a coated n-type thermoelectric semiconductor block 221, and coatedp-type thermoelectric semiconductor block 222 are obtained.

The metal coated layer 223 is either a single layer composed of nickel(Ni), copper (Cu), gold (Au), or the like, or a composite layer composedof single layers stacked up. The metal coated layer 223 is provided inorder to improve electrical connection between various wiring electrodesdescribed hereinafter and thermoelectric semiconductors. It is desirabletherefore to ensure ohmic contact between the metal coated layer 223 andthe n-type thermoelectric semiconductor block 1, as well as the p-typethermoelectric semiconductor block 2, by applying proper heat treatmentto the metal coated layer 223 when or after being formed.

The thickness of the metal coated layers 223 may be in the range ofabout 0.1 to 50 μm. However, in view of the possibility that the heightof the coated n-type thermoelectric semiconductor block 221, and coatedp-type thermoelectric semiconductor block 222, respectively, is madeeven by slightly removing portions of the surfaces of the metal coatedlayers 223 through a polishing process, or the like in a later step ofprocessing, there will arise problems that if the metal coated layers223 are excessively thin, it becomes difficult to apply treatmentthereto due to too little allowance for polishing while if the same areexcessively thick, this is prone to cause a stress-related problem.Accordingly, the thickness of the metal coated layers 223 is preferablyin the range of 2 to 10 μm, and an electrolytic or electroless platingmethod is most suitable for forming a film in a thickness on this order.

In this embodiment, for the metal coated layer 223, a multilayered filmcomposed of the Ni layer and Au layer, 5 μm in total thickness, isformed by the electrolytic plating method.

For the process shown in FIG. 27 and ones thereafter, any selected fromthe processes adopted in the second, fourth, fifth, and sixthembodiments can be applied. The seventh embodiment will be described onthe assumption processes substantially similar to those applied in thefifth embodiment are adopted.

Accordingly, FIG. 28 corresponds to FIG. 23. That is, an n-typethermoelectric semiconductor composite block formed by bonding thecoated n-type thermoelectric semiconductor block 221 to a large base110, and a p-type thermoelectric semiconductor composite block formed bybonding the coated p-type thermoelectric semiconductor block 222 to alarge base 120 are prepared, and longitudinal grooves 16, 26, andlongitudinal partition walls 17, 27 are formed in the coated n-type andp-type thermoelectric semiconductor blocks, respectively, by means ofthe grinding process using a dicing saw, or the polishing process usinga wire saw. As a result, a coated n-type grooved composite block 231,and coated p-type grooved composite block 232 are fabricated. In thisinstance, portions of the respective metal coated layers 223, at theupper or lower ends of the longitudinal partition walls 17, 27, are leftintact as metal layers 233.

The coated n-type thermoelectric semiconductor block 221 and coatedp-type thermoelectric semiconductor block 222 are bonded to the largebase 110 and large base 120, respectively, by use of an adhesive or wax.Further, for the large bases 110 and 120, any material having a hardnessto a given degree such as glass, ceramic, plastics, metal, or the like,may be employed.

The pitch at which the longitudinal grooves 16, 26 are formed, and thewidth and depth of the longitudinal grooves 16, 26 are substantially asdescribed with reference to FIG. 23, except that the depth thereofsomewhat differs. In this embodiment, the longitudinal grooves 16, 26are formed to a depth either of the interface between the coated n-typethermoelectric semiconductor block 221 and the large base 110 or betweenthe coated p-type thermoelectric semiconductor block 222 and the largebase 120, or so as to be cut into the large base 110 or 120.

The reason for this is that in carrying out a process of combining thecoated n-type grooved composite block 231 with the coated p-type groovedcomposite block 232, the surfaces of the metal layers 233 of therespective coated grooved composite blocks are rendered to be flush witheach other.

Subsequently, as described in the fifth embodiment with reference toFIG. 24, the coated n-type grooved composite block 231 and coated p-typegrooved composite block 232 are combined to be fitted to each other, andgaps in fitting parts therebetween are filled with adhesive insulationmembers, forming adhesion layers 32 shown in FIG. 29, so that anintegrated composite block is fabricated through adhesion of the coatedgrooved composite blocks with each other.

Thereafter, a second grooving process is applied to the integratedcomposite block, whereby a grooved integrated composite block withtransverse grooves as well as transverse partition walls formed thereinis formed, and by filling up the respective transverse grooves withinsulating resin and curing the same, insulating resin layers, the sameas the insulating resin layers 54 shown in FIG. 5, are formed.

After removing the large bases 110, 120, a thermoelectric device block 5as shown in FIG. 6 is obtained. Further, by forming respectiveelectrodes 81, 82, as shown in FIG. 29, on both the upper and undersurfaces of the thermoelectric device block, and connecting n-typethermoelectric semiconductor pieces 51 and p-type thermoelectricsemiconductor pieces 52 to each other, alternately and in series, athermoelectric device 80 can be fabricated.

FIG. 29 illustrates the sectional shape of the thermoelectric device 80according to the seventh embodiment of the invention, corresponding tothe plan view shown in FIGS. 9 and 18, respectively. In this connection,for forming the upper surface electrode 81 and the under surfaceelectrode 82, the vapor deposition film described hereinbefore isnormally used. However, the method according to this embodiment may becharacterized by use of an electrically conductive paste such as silverpaste.

Electrical connection between the electrically conductive paste and suchsemiconductor as used in the method of the invention is generally proneto create a problem due to high contact resistance. Therefore, with theconstruction according to the invention, the electrically conductivepaste is not suitable for use for wiring electrodes. However, byproviding the metal layer 233 shown in the seventh embodiment, thecontact resistance described can be reduced to a negligible level.Consequently, the electrically conductive paste can be used for theupper surface electrode 81 and the under surface electrode 82.

The method according to this embodiment has an advantage in thatproductivity is remarkably improved because with the use of theelectrically conductive paste, the electrodes can be formed throughpatterning by use of a screen printing method.

Eighth Embodiment: FIGS. 30 and 31

Next, an eighth embodiment of the method of fabricating a thermoelectricdevice according to the invention is described hereinafter withreference to FIGS. 30 and 31.

The method according to the eighth embodiment is described starting fromthe stage of a thermoelectric device block (for example, the same as thethermoelectric device block 5 shown in FIG. 6) prior to the wiringprocess described in the first to the fifth embodiments. That is,respective processes applied up to this stage in this embodiment are thesame as those in the case of the respective embodiments described above.

After the formation of the thermoelectric device block described above,metal layers 233, the same as in the case of the seventh embodiment, areformed on at least the surfaces of n-type thermoelectric semiconductorpieces 51 and p-type thermoelectric semiconductor pieces 52, wherewiring electrodes are to be formed.

As a result, a thermoelectric device block 253 shown in FIG. 30illustrating the sectional view thereof is fabricated.

In this embodiment, the metal layers 233 are preferably deposited by aplating method whereby a single-layered film composed of Ni, Au, Cu, orthe like, or a multi-layered film composed of the aforesaid films, isformed. In particular, an electroless plating is most suitable wherebyselective plating can be applied to exposed surfaces of thethermoelectric semiconductor pieces 51, 52, taking advantage ofselectivity in the condensation coefficient of Pd (palladium) acting asa catalyst on the surfaces of the thermoelectric semiconductor pieces51, 52, adhesive layers 32, and insulating resin layers 54.

Further, it is preferable not to form the metal layer 233 on the sideaces of the thermoelectric semiconductor pieces on the periphery of thethermoelectric device block (for example, the thermoelectric deviceblock 5 shown in FIG. 6) prior to the wiring process being appliedthereto, which is the starting point of description of this embodiment.Hence, in this embodiment, a coated layer 254 composed of the samematerial as is used for the adhesive layers 32, or the insulating resinlayers 54, is formed on the peripheral face (the side face) of thethermoelectric device block.

FIG. 31 shows a thermoelectric device 80, completed by forming uppersurface electrodes 81 and under surface electrodes 82 on thethermoelectric device block 253 shown in FIG. 30 by use of theelectrically conductive paste as described in the seventh embodiment.

The method according to this embodiment, whereby the metal layers 233are formed at a later stage of processing, has still an advantage inthat productivity is remarkably improved because the electricallyconductive paste can be used as in the case of the seventh embodiment,and the electrodes can be formed through patterning by use of the screenprinting method.

Ninth Embodiment: FIGS. 32 and 33

Next, a ninth embodiment of the method of fabricating a thermoelectricdevice according to the invention is described hereinafter withreference to FIGS. 32 and 33.

FIG. 32 shows a provisional thermoelectric device 270 fabricatedaccording to the ninth embodiment, which is substantially the same asthe thermoelectric device 6, 60, or 80 described in the respectiveembodiments described in the foregoing and fabricated by substantiallythe same processes except that in place of the adhesive layers 32, andthe insulating resin layers 54, provisional fixture layers 271 areprovided therein.

As opposed to the embodiments described in the foregoing, wherein theadhesive layers 32 and the insulating resin layers 54 are among thecomponents of the thermoelectric device in the final form, theinsulating resin layers 54 are not included in the components of thethermoelectric device in the final form in the case of the methodaccording to the ninth embodiment.

Accordingly, in place of the adhesive layers 32 and the insulating resinlayers 54, the provisional fixture layers 271 are formed forprovisionally securing the n-type thermoelectric semiconductor pieces 51and p-type thermoelectric semiconductor pieces 52, and are removed lateron. The provisional fixture layers 271 are formed by filling up gaps inthe fitting parts after the fitting process is applied to the pair ofthe grooved blocks or by filling up the transverse grooves 47 afterbeing formed as shown in FIGS. 4, 13, and the like, with a provisionalfixture material in the same way as for the formation of the adhesivelayers 32, and the insulating resin layers 54. For the provisionalfixture material, an adhesive material removable by heating or by use ofa solvent such as wax is employed.

In the method of fabrication according to the ninth embodiment, anadhesive resin such as epoxy resin is applied as shown in FIG. 33 to theentire upper as well as under surfaces of the provisional thermoelectricdevice 270 shown in FIG. 32, thereby forming insulating fixture layers284. The provisional thermoelectric device 270 is then sandwichedbetween a heat radiation plate 281 and a heat absorption plate 282, andfixedly attached thereto via the insulating fixture layers 284integrally formed.

For the heat radiation plate 281 and heat absorption pate 282, amaterial having high thermal conductivity, that is, a metal or ceramic,is used.

Particularly in the case of a metal being selected for this purpose, atreatment to form an insulating oxide film may preferably be applied tothe surface of the metal because of the risk of an accidental shortcircuit occurring between upper surface electrodes 81 and the heatradiation plate 281, or between under surface electrodes 82 and the heatabsorption plate 282 if the insulating fixture layers 284 is renderedtoo thin.

Thereafter, as shown in FIG. 33, after securing the provisionalthermoelectric device 270 onto the heat radiation plate 281 and heatabsorption plate 282, the provisional fixture layers 271 are removed byuse of heat or a solvent, thereby fabricating a thermoelectric device280 provided with voids 283 created in regions vacated as above.

With the construction of the thermoelectric device 280 according to thisembodiment, heat conduction by materials other than the thermoelectricsemiconductors between the heat radiation plate 281 and the heatabsorption plate 282 is largely inhibited because of the very lowthermal conductivity of the air in the voids 283, enhancing theperformance of the thermoelectric device.

In the aforesaid embodiment, in place of both the adhesive layers 32provided in the fitting parts between the n-type and p-typethermoelectric semiconductor grooved blocks and the insulating resinlayers 54 provided in the transverse grooves formed after the pair ofthe grooved blocks are integrated, the provisional fixture layers 271are provided. However, only either of the adhesive layers or theinsulating resin layers may be substituted by the provisional fixturelayers 271, and after sandwiching the provisional thermoelectric device270 between the heat radiation plate 281 and heat absorption plate 282so as to be integrally secured by the insulating fixture layers 284, theprovisional fixture layers 271 may be removed so that either theadhesive layers 32 or the insulating resin layers 54 are left intact.

This will enable the thermoelectric device to maintain sufficientstrength while enhancing the performance thereof.

With the thermoelectric device 280 shown in FIG. 33, when used forgeneration of power, the heat absorption plate 282 is positioned on thelower temperature side.

Another Embodiment of a Process of Fabricating a ThermoelectricSemiconductor Grooved Block: FIG. 34

Now, another embodiment of a process of fabricating a thermoelectricsemiconductor grooved block according to the invention is describedhereinafter with reference to FIG. 34.

With the first embodiment or the third embodiment describedhereinbefore, in the process of fabricating the n-type and p-typethermoelectric semiconductor grooved blocks, the plurality of groovesparallel with each other are formed in the n-type and p-typethermoelectric semiconductor blocks 1 and 2, respectively, by machiningusing the wire saw or the like, thereby fabricating the n-typethermoelectric semiconductor grooved block 11 and p-type thermoelectricsemiconductor grooved block 21.

However, the n-type thermoelectric semiconductor grooved block 11 andp-type thermoelectric semiconductor grooved block 21 can also befabricated by molding n-type thermoelectric semiconductor material andp-type thermoelectric semiconductor material separately into a mold(metal mold) for the grooved block, and then sintering the moldedmaterials.

In such a process of fabricating the grooved blocks as described above,a compound used for injection molding is produced by adding a mixture asan organic binder, consisting of, for example,ethylene-vinyl-acetate-polybutylmethacrylate-polystyrene copolymer,atactic polypropylene, paraffin wax, and dibutyl phthalate to pulverizedpowders of a thermoelectric semiconductor material (for example, in thecase of the p-type thermoelectric semiconductor material, pulverizedpowders of BiTeSb crystals as in the case of the first embodiment) onthe order of 1 μm in average grain size, and kneading the same with theuse of a pressurized kneader. A suitable mixing ratio of the pulverizedpowders to the organic binder is 5 to 15 wt parts of the organic binderagainst 100 wt parts of the pulverized powders.

The compound for injection molding thus produced is molded by use of aninjection molding machine, and FIG. 34 is a sectional view of a metalmold with which molding is performed.

In this case, the compound for injection molding is pressurized andfilled from a nozzle 304 into a molding cavity 308 formed in the shapeof the grooved block inside a movable mold 301 via a sprue 306 of afixed mold 303 and a gate 307 of an intermediate mold 302.

A molded body formed in the molding cavity 308 as described above ispushed out by ejector pins 305, and taken out after the movable block301 is shifted and separated from the intermediate mold 302. The moldingcavity 308 is designed to have dimensions about 20% larger than those ofthe grooved block to allow for shrinkage occurring to the molded bodyduring the sintering thereof.

The molded bodies are then placed side by side on a flat plate made ofalumina in a vacuum furnace at 400° C. for a retention time of 1 hour,obtaining provisional sintered bodies with organic binders substantiallyremoved. In the final step, the provisional sintered bodies are againplaced side by side on the flat plate made of alumina, and subjected toa sintering process at 470° C. for a duration of 3 hours in an electricfurnace in a hydrogen-flow atmosphere, obtaining sintered bodiescomposed of the n-type or p-type thermoelectric semiconductors,respectively. The sintered bodies are the n-type grooved block 11, andp-type grooved block 21, respectively.

Supplementary Explanation

Various embodiments of the method of fabricating the thermoelectricdevice according to the invention have been described in the foregoing,and every one of the embodiments is based on the construction whereinthe thermoelectric semiconductor pieces 51, 52 are all arranged in amatrix fashion. That is, all the embodiments have made a point ofapplying the process of forming the transverse grooves after the processof forming the longitudinal grooves, then the process of exposing thethermoelectric semiconductor pieces, and further, the process of formingthe electrodes for wiring and the like, thus completing the fabricationof the thermoelectric device.

However, in the case where the thermocouples, even though small innumber, can be effectively utilized, the thermoelectric device may becompleted in the respective embodiments described hereinbefore byapplying the process of exposing the thermoelectric semiconductor pieceswithout applying the process of forming the transverse grooves, andthen, by forming the electrodes for wiring and the like.

In the case of adopting such steps of processing, the finished productwill be the thermoelectric device of a construction wherein thin layerscomposed of n-type and p-type thermoelectric semiconductors,respectively, are alternately arranged and connected to each other inseries.

It is obvious that the method of fabricating the thermoelectric deviceaccording to the invention is sufficiently effective for fabrication ofthe thermoelectric device having the construction described above.

As described in each of the aforesaid embodiments, the longitudinalgrooves as well as the transverse grooves are formed by use of the wiresaw or the dicing saw, and in the case that the grooving process isapplied by a grinding method using the wire saw, the bottom surfaces ofthe longitudinal grooves as well as the transverse grooves become acircular arc in actual shape.

Although the longitudinal grooves have arc-shaped bottom surfaces whilethe longitudinal partition walls have rectangular top ends, there willarise no particular problem when the n-type grooved block is combinedwith the p-type grooved block to be fitted to each other because gapsformed are filled up with the adhesive.

Further, when the transverse grooves are formed by use of the wire sawafter the integrated block has been formed, the bottom surfaces of thetransverse grooves become a circular arc in shape. However, there willarise no problem in this case either, because the transverse grooves arefilled up with the insulating resin.

As is evident from the foregoing description, in the method offabricating the thermoelectric device according to the invention, thegrooved blocks composed of the n-type and p-type thermoelectricsemiconductors, respectively, are fabricated by applying a precisionmachining process to thermoelectric semiconductor members, or byapplying a precision molding process to thermoelectric semiconductormaterial, and then, by applying an integration process of combining thegrooved blocks so as to be fitted to each other, the thermoelectricsemiconductor members can always be handled in the form of a unit(block). Hence, the thermoelectric device incorporating thethermocouples composed of a multitude of thermoelectric semiconductorpieces can be fabricated without applying processes such as a process offorming thermoelectric semiconductors into a thin sheet-like shape, aprocess of forming thermoelectric semiconductors into a kenzan-likeshape by applying a fine grooving process, and the like wherein thethermoelectric semiconductor materials are susceptible to undergobreakage.

Accordingly, an ultra small thermoelectric device capable of outputtinga high voltage can be fabricated easily and efficiently, making itpossible to utilize power generated by temperature differences occurringin a portable electronic device such as a wrist watch.

INDUSTRIAL APPLICABILITY

With the method of fabricating a thermoelectric device according to theinvention, a thermoelectric device small in size, incorporating amultitude of thermocouples formed therein, and capable of outputting ahigh voltage can be fabricated easily and efficiently. As a high outputvoltage can be produced by putting the thermoelectric device to use as asmall thermoelectric generator, the thermoelectric device installed in aportable miniature electronic device such as a wrist watch and the likecan be used as a power supply for electric power generated bytemperature differences.

The thermoelectric device can also be used in fabrication of a highperformance cooling system of small size, which is quite useful as aportable refrigerator, or a localized cooler for lasers, integratedcircuits, and the like.

What is claimed is:
 1. A method of fabricating a thermoelectric devicecomprising: a first grooving process applied to an n-type thermoelectricsemiconductor composite block prepared by bonding an n-typethermoelectric semiconductor block to a base and a p-type thermoelectricsemiconductor composite block prepared by bonding a p-typethermoelectric semiconductor block to a base, for forming a plurality ofgrooves in the n-type thermoelectric semiconductor block and the p-typethermoelectric semiconductor block, respectively, at a same pitch inonly one direction, and to a depth close to the interface between therespective thermoelectric semiconductor blocks and the base thereof; afitting process of fitting the n-type thermoelectric semiconductorcomposite block and p-type thermoelectric semiconductor composite block,with the grooves formed by said first grooving process, respectively, toeach other such that respective grooved surfaces face each other; anadhesion process of forming an integrated block by filling gaps infitting parts between the n-type thermoelectric semiconductor compositeblock and the p-type thermoelectric semiconductor composite block,fitted to each other by said fitting process, with adhesive insulationmembers so as to adhere the n-type thermoelectric semiconductorcomposite block and the p-type thermoelectric semiconductor compositeblock to each other; a second grooving process of forming a plurality ofgrooves in the direction crossing the direction of the grooves formed bysaid first grooving process, and to a depth close to the interfacebetween the respective thermoelectric semiconductor blocks and the basethereof in the integrated block formed by said adhesion process; asolidification process of filling up the grooves formed by said secondgrooving process with insulation members, and solidifying the same; anda thermoelectric semiconductor pieces exposure process of exposingn-type and p-type thermoelectric semiconductor pieces by removing therespective bases of the integrated blocks wherein the grooves are filledwith the insulation member and the insulation member is then solidifiedin said solidification process; characterized in that the bases of then-type thermoelectric semiconductor composite block and the p-typethermoelectric semiconductor composite block, respectively, have asurface area larger than an area of a bonded portion of the surface ofthe respective thermoelectric semiconductor blocks, and in the fittingprocess, spacers are interposed between portions of the bases of then-type thermoelectric semiconductor composite block and the p-typethermoelectric semiconductor composite block, respectively, where therespective thermoelectric semiconductor blocks do not exist, so that aspacing between the bases is controlled to be substantially equivalentto thickness of the respective thermoelectric semiconductor blocks.
 2. Amethod of fabricating a thermoelectric device according to claim 1,further comprising an electrode forming process of forming electrodesfor connecting the exposed n-type and p-type thermoelectricsemiconductor pieces to each other alternately and in series, appliedafter the thermoelectric semiconductor pieces exposure process.
 3. Amethod of fabricating a thermoelectric device according to claim 1,characterized in that before the n-type thermoelectric semiconductorblock and the p-type thermoelectric semiconductor block are bonded tothe bases, respectively, a metal coated layer is formed on the surfaceof the respective thermoelectric semiconductor blocks, bonded to therespective bases, and on the surface thereof on the opposite side.
 4. Amethod of fabricating a thermoelectric device according to claim 3,further comprising an electrode formation process of forming electrodesfor connecting the exposed n-type and p-type thermoelectricsemiconductor pieces to each other alternately and in series by use ofan electrically conductive paste applied on the metal coated layer afterthe thermoelectric semiconductor pieces exposure process.
 5. A method offabricating thermoelectric device comprising: a first grooving processapplied to two n-type thermoelectric semiconductor composite blocksprepared by bonding an n-type thermoelectric semiconductor block to abase, respectively, and two p-type thermoelectric semiconductorcomposite blocks prepared by bonding a p-type thermoelectricsemiconductor block to a base, respectively, for forming a plurality ofgrooves at a same pitch, and to a depth close to the interface betweenthe respective thermoelectric semiconductor blocks and the base thereof,in the n-type thermoelectric semiconductor block and the n-typethermoelectric semiconductor block, respectively; a first fittingprocess of fitting the two pairs of the n-type thermoelectricsemiconductor composite block and the p-type thermoelectricsemiconductor composite block, with the grooves formed therein,respectively, by said first grooving process to each other,respectively, such that respective grooved surfaces face each other; afirst adhesion process of forming two integrated blocks by adhering thetwo pairs of the n-type thermoelectric semiconductor composite blocksand p-type thermoelectric semiconductor composite blocks to each other,respectively, by filling gaps in fitting parts between the respectiven-type thermoelectric semiconductor composite blocks and p-typethermoelectric semiconductor composite blocks, fitted to each other bysaid first fitting process, with adhesive insulation members; a secondgrooving process of forming two grooved integrated blocks by forming aplurality of grooves at a same pitch in the two integrated blocksformed, respectively, by said first adhesion process, in the directioncrossing the direction of the grooves formed by said first groovingprocess, and to a depth close to an interface between the respectivethermoelectric semiconductor blocks and the base thereof; a secondfitting process of fitting the two grooved integrated blocks to eachother such that respective grooved surfaces face each other; a secondadhesion process of forming a second integrated block by adhering thetwo grooved integrated blocks, fitted to each other by said secondfitting process, to each by filling gaps in fitting parts between thetwo grooved integrated blocks with adhesive insulation members; and athermoelectric semiconductor pieces exposure process of exposing n-typeand p-type thermoelectric semiconductor pieces by removing therespective bases of the second integrated block; characterized in thebases having a surface area larger than an area of a bonded portion ofthe surface of the respective thermoelectric semiconductor blocks areused for the base of the n-type thermoelectric semiconductor compositeblock and the p-type thermoelectric semiconductor composite block,respectively, and spacers are interposed between portions of therespective basis of the n-type thermoelectric semiconductor compositeblock and the p-type thermoelectric semiconductor composite block to befitted to each other, where the respective thermoelectric semiconductorblocks do not exist, controlling a spacing between the bases to besubstantially equivalent to thicknesses of the respective thermoelectricsemiconductor blocks in the first fitting process, spacers being furtherinterposed between portions of the respective basis of the twointegrated grooved blocks to be fitted to each other, where therespective thermoelectric semiconductor blocks do not exist, controllinga spacing between the bases to be substantially equivalent to thethickness of the respective thermoelectric semiconductor blocks in thesecond fitting process.
 6. A method of fabricating a thermoelectricdevice according to claim 5, further comprising an electrode formingprocess of forming electrodes for connecting the exposed n-type andp-type thermoelectric semiconductor pieces to each other alternately andin series, applied after the thermoelectric semiconductor piecesexposure process.
 7. A method of fabricating a thermoelectric deviceaccording to claim 5, characterized in that before the n-typethermoelectric semiconductor block and the p-type thermoelectricsemiconductor block are bonded to the bases, respectively, a metalcoated layer is formed on the surface of the respective thermoelectricsemiconductor blocks, bonded to the respective bases, and on the surfacethereof on the opposite side.
 8. A method of fabricating athermoelectric device according to claim 7, further comprising anelectrode formation process of forming electrodes for connecting theexposed n-type and p-type thermoelectric semiconductor pieces to eachother alternately and in series by use of an electrically conductivepaste applied on the metal coated layer after the thermoelectricsemiconductor pieces exposure process.
 9. A method of fabricating athermoelectric device, comprising: a grooved block fabrication processof forming grooved blocks composed of an n-type thermoelectricsemiconductor and p-type thermoelectric semiconductor, respectively,each provided with a plurality of grooves formed at a same pitch andparallel with each other, leaving a depthwise portion of respectivegrooved blocks intact; a fitting process of fitting the grooved blockscomposed of the n-type thermoelectric semiconductor and p-typethermoelectric semiconductor formed, respectively, by said grooved blockfabrication process to each other such that surfaces of the respectivegrooved blocks, with the grooves formed thereon, face each other; anadhesion process of forming an integrated block by adhering the groovedblock composed of the n-type thermoelectric semiconductor and thegrooved block composed of the p-type thermoelectric semiconductor,fitted to each other by said fitting process, to each other afterfilling up gaps in fitting parts between the respective grooved blockswith an adhesive insulation member; and a thermoelectric semiconductorpieces exposure process of exposing n-type and p-type thermoelectricsemiconductor pieces by removing all portions of the integrated blockformed by said adhesion process, other than the fitting parts where thegrooved block composed of the n-type thermoelectric semiconductor andthe grooved block composed of the p-type thermoelectric semiconductorare fitted to each other; characterized in that the insulation memberfor filling up the gaps in the fitting parts in the adhesion process isan adhesive insulation member with insulating spacers dispersed therein.10. A method of fabricating a thermoelectric device comprising: agrooved block fabrication process of forming grooved blocks composed ofan n-type thermoelectric semiconductor and a p-type thermoelectricsemiconductor, respectively, each provided with a plurality of groovesformed at a same pitch and parallel with each other in only onedirection, leaving a depthwise portion of respective grooved blocksintact; a fitting process of fitting the grooved blocks composed of then-type thermoelectric semiconductor and the p-type thermoelectricsemiconductor formed, respectively, by said grooved block fabricationprocess to each other such that surfaces of the respective groovedblocks, with the grooves formed thereon, face each other; an adhesionprocess of forming an integrated block by adhering the grooved blockcomposed of the n-type thermoelectric semiconductor and the groovedblock composed of the p-type thermoelectric semiconductor, fitted toeach other by said fitting process, to each other after filling up gapsin fitting parts between the respective grooved blocks with an adhesiveinsulation member; a second grooving process of forming a plurality ofgrooves in the integrated block formed by said adhesion process, in thedirection crossing the direction of the grooves formed by said groovedblock fabrication process, leaving a depthwise portion of the integratedblock intact; a solidification process of filling up the grooves formedby said second grooving process with an adhesive insulation member andsolidifying the same; and a thermoelectric semiconductor pieces exposureprocess of exposing n-type and p-type thermoelectric semiconductorpieces by removing all portions of the integrated block wherein theadhesive insulation member filling up the grooves is solidified in saidsolidification process, other than the fitting parts where the groovedblock composed of the n-type thermoelectric semiconductor and thegrooved block composed of the p-type thermoelectric semiconductor arefitted to each other; characterized in that the insulation member forfilling up the gaps in the fitting parts in the adhesion process is anadhesive insulation member with insulating spacers dispersed therein.11. A method of fabricating a thermoelectric device comprising: a firstgrooving process applied to an n-type thermoelectric semiconductorcomposite block prepared by bonding an n-type thermoelectricsemiconductor block to a base and a p-type thermoelectric semiconductorcomposite block prepared by bonding a p-type thermoelectricsemiconductor block to a base, for forming a plurality of grooves in then-type thermoelectric semiconductor block and the p-type thermoelectricsemiconductor block, respectively, at a same pitch in only onedirection, and to a depth close to the interface between the respectivethermoelectric semiconductor blocks and the base thereof; a fittingprocess of fitting the n-type thermoelectric semiconductor compositeblock and p-type thermoelectric semiconductor composite block, with thegrooves formed by said first grooving process, respectively, to eachother such that respective grooved surfaces face each other; an adhesionprocess of forming an integrated block by filling gaps in fitting partsbetween the n-type thermoelectric semiconductor composite block and thep-type thermoelectric semiconductor composite block, fitted to eachother by said fitting process, with adhesive insulation members so as toadhere the n-type thermoelectric semiconductor composite block and thep-type thermoelectric semiconductor composite block to each other; asecond grooving process of forming a plurality of grooves in thedirection crossing the direction of the grooves formed by said firstgrooving process, and to a depth close to the interface between therespective thermoelectric semiconductor blocks and the base thereof inthe integrated block formed by said adhesion process; a solidificationprocess of filling up the grooves formed by said second grooving processwith insulation members, and solidifying the same; and a thermoelectricsemiconductor pieces exposure process of exposing n-type and p-typethermoelectric semiconductor pieces by removing the respective bases ofthe integrated blocks wherein the grooves are filled with the insulationmember and the insulation member is then solidified in saidsolidification process; characterized in that the insulation member forfilling up the gaps in the fitting parts in the adhesion process is anadhesive insulation member with insulating spacers dispersed therein.12. A method of fabricating a thermoelectric device comprising: agrooved block fabrication process of forming two pairs of grooved blockscomposed of an n-type thermoelectric semiconductor and a p-typethermoelectric semiconductor, respectively, provided with a plurality ofgrooves formed at a same pitch and parallel with each other,respectively, leaving a depthwise portion of respective grooved blocksintact; a first fitting process of fitting each pair of the groovedblocks composed of the n-type thermoelectric semiconductor and thegrooved block of the p-type thermoelectric semiconductor, formed by saidgrooved block fabrication process, to each other such that surfaces withthe grooves formed thereon face each other; a first adhesion process offorming two integrated blocks by filling up gaps in fitting partsbetween each pair of the grooved blocks composed of the n-typethermoelectric semiconductor and the p-type thermoelectricsemiconductor, respectively, fitted to each other by said first fittingprocess, with adhesive insulation members, and solidifying the same; agrooving process of forming two grooved integrated blocks by forming ineach of the two integrated blocks a plurality of grooves at a same pitchand in the direction crossing the direction of the grooves formed bysaid grooved block fabrication process, leaving a depthwise portion ofrespective integrated blocks intact; a second fitting process of fittingthe two grooved integrated blocks to each other such that surfaces withthe grooves thus formed thereon face each other; a second adhesionprocess of forming a second integrated block by filling gaps in fittingparts between the two grooved integrated blocks fitted to each other bysaid fitting process with adhesive insulation members, and solidifyingthe same; and a thermoelectric semiconductor pieces exposure process ofexposing n-type and p-type thermoelectric semiconductor pieces byremoving all depthwise portions of the second integrated block, otherthan the fitting parts; characterized in that the insulation member forfilling up the gaps in the fitting parts in at least either of the firstadhesion process or the second adhesion process is an adhesiveinsulation member with insulating spacers dispersed therein.
 13. Amethod of fabricating thermoelectric device comprising: a first groovingprocess applied to two n-type thermoelectric semiconductor compositeblocks prepared by bonding an n-type thermoelectric semiconductor blockto a base, respectively, and two p-type thermoelectric semiconductorcomposite blocks prepared by bonding a p-type thermoelectricsemiconductor block to a base, respectively, for forming a plurality ofgrooves at a same pitch, and to a depth close to the interface betweenthe respective thermoelectric semiconductor blocks and the base thereof,in the n-type thermoelectric semiconductor block and the p-typethermoelectric semiconductor block, respectively; a first fittingprocess of fitting the two pairs of the n-type thermoelectricsemiconductor composite block and the p-type thermoelectricsemiconductor composite block, with the grooves formed therein,respectively, by said first grooving process to each other,respectively, such that respective grooved surfaces face each other; afirst adhesion process of forming two integrated blocks by adhering thetwo pairs of the n-type thermoelectric semiconductor composite blocksand p-type thermoelectric semiconductor composite blocks to each other,respectively, by filling gaps in fitting parts between the respectiven-type thermoelectric semiconductor composite blocks and p-typethermoelectric semiconductor composite blocks, fitted to each other bysaid first fitting process, with adhesive insulation members; a secondgrooving process of forming two grooved integrated blocks by forming aplurality of grooves at a same pitch in the two integrated blocksformed, respectively, by said first adhesion process, in the directioncrossing the direction of the grooves formed by said first groovingprocess, and to a depth close to an interface between the respectivethermoelectric semiconductor blocks and the base thereof; a secondfitting process of fitting the two grooved integrated blocks to eachother such that respective grooved surfaces face each other; a secondadhesion process of forming a second integrated block by adhering thetwo grooved integrated blocks, fitted to each other by said secondfitting process, to each by filling in fitting parts between the twogrooved integrated blocks with adhesive insulation members; and athermoelectric semiconductor pieces exposure process of exposing n-typeand p-type thermoelectric semiconductor pieces by removing therespective bases of the second integrated block; characterized in thatthe insulation member for filling up the gaps in the fitting parts in atleast either of the first adhesion process or the second adhesionprocess is an adhesive insulation member with insulating spacersdispersed therein.
 14. A method of fabricating a thermoelectric devicecomprising: a first grooving process applied to an n-type thermoelectricsemiconductor composite block prepared by bonding an n-typethermoelectric semiconductor block to a base and a p-type thermoelectricsemiconductor composite block prepared by bonding a p-typethermoelectric semiconductor block to a base, for forming a plurality ofgrooves in the n-type thermoelectric semiconductor block and the p-typethermoelectric semiconductor block, respectively, at a same pitch inonly one direction, and to a depth close to the interface between therespective thermoelectric semiconductor blocks and the base thereof; afitting process of fitting the n-type thermoelectric semiconductorcomposite block and p-type thermoelectric semiconductor composite block,with the grooves formed by said first grooving process, respectively, toeach other such that respective grooved surfaces face each other; anadhesion process of forming an integrated block by filling gaps infitting parts between the n-type thermoelectric semiconductor compositeblock and the p-type thermoelectric semiconductor composite block,fitted to each other by said fitting process, with adhesive insulationmembers so as to adhere the n-type thermoelectric semiconductorcomposite block and the p-type thermoelectric semiconductor compositeblock to each other; a second grooving process of forming a plurality ofgrooves in the direction crossing the direction of the grooves formed bysaid first grooving process, and to a depth close to the interfacebetween the respective thermoelectric semiconductor blocks and the basethereof in the integrated block formed by said adhesion process; asolidification process of filling up the grooves formed by said secondgrooving process with insulation members, and solidifying the same; anda thermoelectric semiconductor pieces exposure process of exposingn-type and p-type thermoelectric semiconductor pieces by removing therespective bases of the integrated blocks wherein the grooves are filledwith the insulation member and the insulation member is then solidifiedin said solidification process; characterized in that before the n-typethermoelectric semiconductor block and the p-type thermoelectricsemiconductor are bonded to the bases, respectively, a metal coatedlayer is formed on the surface of the respective thermoelectricsemiconductor blocks, bonded to the respective bases, and on the surfacethereof on the opposite side.
 15. A method of fabricating athermoelectric device according to claim 14, further comprising anelectrode formation process of forming electrodes for connecting theexposed n-type and p-type thermoelectric semiconductor pieces to eachother alternately and in series by use of an electrically conductivepaste applied on the metal coated layer after the thermoelectricsemiconductor pieces exposure process.
 16. A method of fabricatingthermoelectric device comprising: a first grooving process applied totwo n-type thermoelectric semiconductor composite blocks prepared bybonding an n-type thermoelectric semiconductor block to a base,respectively, and two p-type thermoelectric semiconductor compositeblocks prepared by bonding a p-type thermoelectric semiconductor blockto a base, respectively, for forming a plurality of grooves at a samepitch, and to a depth close to the interface between the respectivethermoelectric semiconductor blocks and the base thereof, in the n-typethermoelectric semiconductor block and the p-type thermoelectricsemiconductor block, respectively; a first fitting process of fittingthe two pairs of the n-type thermoelectric semiconductor composite blockand the p-type thermoelectric semiconductor composite block, with thegrooves formed therein, respectively, by said first grooving process toeach other, respectively, such that respective grooved surfaces faceeach other; a first adhesion process of forming two integrated blocks byadhering the two pairs of the n-type thermoelectric semiconductorcomposite blocks and p-type thermoelectric semiconductor compositeblocks to each other, respectively, by filling gaps in fitting partsbetween the respective n-type thermoelectric semiconductor compositeblocks and p-type thermoelectric semiconductor composite blocks, fittedto each other by said first fitting process, with adhesive insulationmembers; a second grooving process of forming two grooved integratedblocks by forming a plurality of grooves at a same pitch in the twointegrated blocks formed, respectively, by said first adhesion process,in the direction crossing the direction of the grooves formed by saidfirst grooving process, and to a depth close to an interface between therespective thermoelectric semiconductor blocks and the base thereof; asecond fitting process of fitting the two grooved integrated blocks toeach other such that respective grooved surfaces face each other; asecond adhesion process of forming a second integrated block by adheringthe two grooved integrated blocks, fitted to each other by said secondfitting process, to each by filling gaps in fitting parts between thetwo grooved integrated blocks with adhesive insulation members; and athermoelectric semiconductor pieces exposure process of exposing n-typeand p-type thermoelectric semiconductor pieces by removing therespective bases of the second integrated block; characterized in thatbefore the n-type thermoelectric semiconductor block and the p-typethermoelectric semiconductor are bonded to the bases, respectively, ametal coated layer is formed on the surface of the respectivethermoelectric semiconductor blocks, bonded to the respective bases, andon the surface thereof on the opposite side.
 17. A method of fabricatinga thermoelectric device according to claim 16, further comprising anelectrode formation process of forming electrodes for connecting theexposed n-type and p-type thermoelectric semiconductor pieces to eachother alternately and in series by use of an electrically conductivepaste applied on the metal coated layer after the thermoelectricsemiconductor pieces exposure process.
 18. A method of fabricating athermoelectric device comprising: a grooved block fabrication process offorming grooved blocks composed of an n-type thermoelectricsemiconductor and a p-type thermoelectric semiconductor, respectively,each provided with a plurality of grooves formed at a same pitch andparallel with each other in only one direction, leaving a depthwiseportion of respective grooved blocks intact; a fitting process offitting the grooved blocks composed of the n-type thermoelectricsemiconductor and the p-type thermoelectric semiconductor formed,respectively, by said grooved block fabrication process to each othersuch that surfaces of the respective grooved blocks, with the groovesformed thereon, face each other; an adhesion process of forming anintegrated block by adhering the grooved block composed of the n-typethermoelectric semiconductor and the grooved block composed of thep-type thermoelectric semiconductor, fitted to each other by saidfitting process, to each other after filling up gaps in fitting partsbetween the respective grooved blocks with an adhesive insulationmember; a second grooving process of forming a plurality of grooves inthe integrated block formed by said adhesion process, in the directioncrossing the direction of the grooves formed by said grooved blockfabrication process, leaving a depthwise portion of the integrated blockintact; a solidification process of filling up the grooves formed bysaid second grooving process with an adhesive insulation member andsolidifying the same; and a thermoelectric semiconductor pieces exposureprocess of exposing n-type and p-type thermoelectric semiconductorpieces by removing all portions of the integrated block wherein theadhesive insulation member filling up the grooves is solidified in saidsolidification process, other than the fitting parts where the groovedblock composed of the n-type thermoelectric semiconductor and thegrooved block composed of the p-type thermoelectric semiconductor arefitted to each other; further comprising a metal layer formation processof forming metal layers on respective surfaces of the exposed n-type andp-type thermoelectric semiconductor pieces, where the electrodes areformed, and an electrode formation process of forming the electrodes forconnecting the exposed n-type and p-type thermoelectric semiconductorpieces to each other alternatively and in series over the metal layers,said processes being applied after the thermoelectric semiconductorpieces exposure process; characterized in that the electrodes are formedby use of an electrically conductive paste in the electrode formationprocess.
 19. A method of fabricating a thermoelectric device comprising:a grooved block fabrication process of forming two pairs of groovedblocks composed of an n-type thermoelectric semiconductor and a p-typethermoelectric semiconductor, respectively, provided with a plurality ofgrooves formed at a same pitch and parallel with each other,respectively, leaving a depthwise portion of respective grooved blocksintact; a first fitting process of fitting each pair of the groovedblocks composed of the n-type thermoelectric semiconductor and thegrooved block of the p-type thermoelectric semiconductor, formed by saidgrooved block fabrication process, to each other such that surfaces withthe grooves formed thereon face each other; a first adhesion process offorming two integrated blocks by filling up gaps in fitting partsbetween each pair of the grooved blocks composed of the n-typethermoelectric semiconductor and the p-type thermoelectricsemiconductor, respectively, fitted to each other by said first fittingprocess, with adhesive insulation members, and solidifying the same; agrooving process of forming two grooved integrated blocks by forming ineach of the two integrated blocks a plurality of grooves at a same pitchand in the direction crossing the direction of the grooves formed bysaid grooved block fabrication process, leaving a depthwise portion ofrespective integrated blocks intact; a second fitting process of fittingthe two grooved integrated blocks to each other such that surfaces withthe grooves thus formed thereon face each other; a second adhesionprocess of forming a second integrated block by filling gaps in fittingparts between the two grooved integrated blocks fitted to each other bysaid fitting process with adhesive insulation members, and solidifyingthe same; and a thermoelectric semiconductor pieces exposure process ofexposing n-type and p-type thermoelectric semiconductor pieces byremoving all depthwise portions of the second integrated block, otherthan the fitting parts; further comprising a metal layer formationprocess of forming metal layers on respective surfaces of the exposedn-type and p-type thermoelectric semiconductor pieces, where theelectrodes are formed, and an electrode formation process of forming theelectrodes for connecting the exposed n-type and p-type thermoelectricsemiconductor pieces to each other alternatively and in series over themetal layers, said processes being applied after the thermoelectricsemiconductor pieces exposure process; characterized in that theelectrodes are formed by use of an electrically conductive paste in theelectrode formation process.
 20. A method of fabricating athermoelectric device comprising: a first grooving process applied to ann-type thermoelectric semiconductor composite block prepared by bondingan n-type thermoelectric semiconductor block to a base and a p-typethermoelectric semiconductor composite block prepared by bonding ap-type thermoelectric semiconductor block to a base, for forming aplurality of grooves in the n-type thermoelectric semiconductor blockand the p-type thermoelectric semiconductor block, respectively, at asame pitch in only one direction, and to a depth close to the interfacebetween the respective thermoelectric semiconductor blocks and the basethereof; a fitting process of fitting the n-type thermoelectricsemiconductor composite block and p-type thermoelectric semiconductorcomposite block, with the grooves formed by said first grooving process,respectively, to each other such that respective grooved surfaces faceeach other; an adhesion process of forming an integrated block byfilling gaps in fitting parts between the n-type thermoelectricsemiconductor composite block and the p-type thermoelectricsemiconductor composite block, fitted to each other by said fittingprocess, with adhesive insulation members so as to adhere the n-typethermoelectric semiconductor composite block and the p-typethermoelectric semiconductor composite block to each other; a secondgrooving process of forming a plurality of grooves in the directioncrossing the direction of the grooves formed by said first groovingprocess, and to a depth close to the interface between the respectivethermoelectric semiconductor blocks and the base thereof in theintegrated block formed by said adhesion process; a solidificationprocess of filling up the grooves formed by said second grooving processwith insulation members, and solidifying the same; and a thermoelectricsemiconductor pieces exposure process of exposing n-type and p-typethermoelectric semiconductor pieces by removing the respective bases ofthe integrated blocks wherein the grooves are filled with the insulationmember and the insulation member is then solidified in saidsolidification process; further comprising a metal layer formationprocess of forming metal layers on respective surfaces of the exposedn-type and p-type thermoelectric semiconductor pieces, where theelectrodes are formed, and an electrode formation process of forming theelectrodes for connecting the exposed n-type and p-type thermoelectricsemiconductor pieces to each other alternatively and in series over themetal layers, said processes being applied after the thermoelectricsemiconductor pieces exposure process; characterized in that theelectrodes are formed by use of an electrically conductive paste in theelectrode formation process.
 21. A method of fabricating thermoelectricdevice comprising: a first grooving process applied to two n-typethermoelectric semiconductor composite blocks prepared by bonding ann-type thermoelectric semiconductor block to a base, respectively, andtwo p-type thermoelectric semiconductor composite blocks prepared bybonding a p-type thermoelectric semiconductor block to a base,respectively, for forming a plurality of grooves at a same pitch, and toa depth close to the interface between the respective thermoelectricsemiconductor blocks and the base thereof, in the n-type thermoelectricsemiconductor block and the p-type thermoelectric semiconductor block,respectively; a first fitting process of fitting the two pairs of then-type thermoelectric semiconductor composite block and the p-typethermoelectric semiconductor composite block, with the grooves formedtherein, respectively, by said first grooving process to each other,respectively, such that respective grooved surfaces face each other; afirst adhesion process of forming two integrated blocks by adhering thetwo pairs of the n-type thermoelectric semiconductor composite blocksand p-type thermoelectric semiconductor composite blocks to each other,respectively, by filling gaps in fitting parts between the respectiven-type thermoelectric semiconductor composite blocks and p-typethermoelectric semiconductor composite blocks, fitted to each other bysaid first fitting process, with adhesive insulation members; a secondgrooving process of forming two grooved integrated blocks by forming aplurality of grooves at a same pitch in the two integrated blocksformed, respectively, by said first adhesion process, in the directioncrossing the direction of the grooves formed by said first groovingprocess, and to a depth close to an interface between the respectivethermoelectric semiconductor blocks and the base thereof; a secondfitting process of fitting the two grooved integrated blocks to eachother such that respective grooved surfaces face each other; a secondadhesion process of forming a second integrated block by adhering thetwo grooved integrated blocks, fitted to each other by said secondfitting process, to each by filling in fitting parts between the twogrooved integrated blocks with adhesive insulation members; and athermoelectric semiconductor pieces exposure process of exposing n-typeand p-type thermoelectric semiconductor pieces by removing therespective bases of the second integrated block; further comprising ametal layer formation process of forming metal layers on respectivesurfaces of the exposed n-type and p-type thermoelectric semiconductorpieces, where the electrodes are formed, and an electrode formationprocess of forming the electrodes for connecting the exposed n-type andp-type thermoelectric semiconductor pieces to each other alternativelyand in series over the metal layers, said processes being applied afterthe thermoelectric semiconductor pieces exposure process; characterizedin that the electrodes are formed by use of an electrically conductivepaste in the electrode formation process.
 22. A method of fabricating athermoelectric device, comprising: a grooved block fabrication processof forming grooved blocks composed of an n-type thermoelectricsemiconductor and p-type thermoelectric semiconductor, respectively,each provided with a plurality of grooves formed at a same pitch andparallel with each other, leaving a depthwise portion of respectivegrooved blocks intact; a fitting process of fitting the grooved blockscomposed of the n-type thermoelectric semiconductor and p-typethermoelectric semiconductor formed, respectively, by said grooved blockfabrication process to each other such that surfaces of the respectivegrooved blocks, with the grooves formed thereon, face each other; anadhesion process of forming an integrated block by adhering the groovedblock composed of the n-type thermoelectric semiconductor and thegrooved block composed of the p-type thermoelectric semiconductor,fitted to each other by said fitting process, to each other afterfilling up gaps in fitting parts between the respective grooved blockswith an adhesive insulation member; and a thermoelectric semiconductorpieces exposure process of exposing n-type and p-type thermoelectricsemiconductor pieces by removing all portions of the integrated blockformed by said adhesion process, other than the fitting parts where thegrooved block composed of the n-type thermoelectric semiconductor andthe grooved block composed of the p-type thermoelectric semiconductorare fitted to each other; characterized in that provisional fixturelayers as insulation members for filling up the gaps in the fittingparts are formed using a material removable by heating or by use of asolvent in the adhesion process; said method further comprising anelectrode formation process of forming electrodes for connecting theexposed n-type and p-type thermoelectric semiconductor pieces to eachother alternately and in series after the thermoelectric semiconductorpieces exposure process, fabricating a provisional thermoelectricdevice, and thereafter performing a process of fixedly attaching a heatradiation plate to one of the surfaces of the provisional thermoelectricdevice, where the electrodes are formed, and a heat absorption plate tothe other via an insulating fixture layer, respectively, and a processof removing the provisional fixture layers either by heating or by useof a solvent after said preceding process.
 23. A method of fabricating athermoelectric device comprising: a grooved block fabrication process offorming grooved blocks composed of an n-type thermoelectricsemiconductor and a p-type thermoelectric semiconductor, respectively,each provided with a plurality of grooves formed at a same pitch andparallel with each other in only one direction, leaving a depthwiseportion of respective grooved blocks intact; a fitting process offitting the grooved blocks composed of the n-type thermoelectricsemiconductor and the p-type thermoelectric semiconductor formed,respectively, by said grooved block fabrication process to each othersuch that surfaces of the respective grooved blocks, with the groovesformed thereon, face each other; an adhesion process of forming anintegrated block by adhering the grooved block composed of the n-typethermoelectric semiconductor and the grooved block composed of thep-type thermoelectric semiconductor, fitted to each other by saidfitting process, to each other after filling up gaps in fitting partsbetween the respective grooved blocks with an adhesive insulationmember; a second grooving process of forming a plurality of grooves inthe integrated block formed by said adhesion process, in the directioncrossing the direction of the grooves formed by said grooved blockfabrication process, leaving a depthwise portion of the integrated blockintact; a solidification process of filling up the grooves formed bysaid second grooving process with an adhesive insulation member andsolidifying the same; and a thermoelectric semiconductor pieces exposureprocess of exposing n-type and p-type thermoelectric semiconductorpieces by removing all portions of the integrated block wherein theadhesive insulation member filling up the grooves is solidified in saidsolidification process, other than the fitting parts where the groovedblock composed of the n-type thermoelectric semiconductor and thegrooved block composed of the p-type thermoelectric semiconductor arefitted to each other; characterized in that provisional fixture layersare formed using a material removable by heating or by use of a solventas at least either of the insulation members for filling up the gaps inthe fitting parts in the adhesion process or the insulation members forfilling up the grooves in the solidification process; said methodfurther comprising an electrode formation process of forming electrodesfor connecting the exposed n-type and p-type thermoelectricsemiconductor pieces to each other alternately and in series after thethermoelectric semiconductor pieces exposure process, fabricating aprovisional thermoelectric device, and thereafter performing a processof fixedly attaching a heat radiation plate to one of the surfaces ofthe provisional thermoelectric device, where the electrodes are formed,and a heat absorption plate to the other via an insulating fixturelayer, respectively, and a process of removing the provisional fixturelayers either by heating or by use of a solvent after said precedingprocess.
 24. A method of fabricating a thermoelectric device comprising:a first grooving process applied to an n-type thermoelectricsemiconductor composite block prepared by bonding an n-typethermoelectric semiconductor block to a base and a p-type thermoelectricsemiconductor composite block prepared by bonding a p-typethermoelectric semiconductor block to a base, for forming a plurality ofgrooves in the n-type thermoelectric semiconductor block and the p-typethermoelectric semiconductor block, respectively, at a same pitch inonly one direction, and to a depth close to the interface between therespective thermoelectric semiconductor blocks and the base thereof; afitting process of fitting the n-type thermoelectric semiconductorcomposite block and p-type thermoelectric semiconductor composite block,with the grooves formed by said first grooving process, respectively, toeach other such that respective grooved surfaces face each other; anadhesion process of forming an integrated block by filling gaps infitting parts between the n-type thermoelectric semiconductor compositeblock and the p-type thermoelectric semiconductor composite block,fitted to each other by said fitting process, with adhesive insulationmembers so as to adhere the n-type thermoelectric semiconductorcomposite block and the p-type thermoelectric semiconductor compositeblock to each other; a second grooving process of forming a plurality ofgrooves in the direction crossing the direction of the grooves formed bysaid first grooving process, and to a depth close to the interfacebetween the respective thermoelectric semiconductor blocks and the basethereof in the integrated block formed by said adhesion process; asolidification process of filling up the grooves formed by said secondgrooving process with insulation members, and solidifying the same; anda thermoelectric semiconductor pieces exposure process of exposingn-type and p-type thermoelectric semiconductor pieces by removing therespective bases of the integrated blocks wherein the grooves are filledwith the insulation member and the insulation member is then solidifiedin said solidification process; characterized in that provisionalfixture layers are formed using a material removable by heating or byuse of a solvent as at least either of the insulation members forfilling up the gaps in the fitting parts in the adhesion process or theinsulation members for filling up the grooves in the solidificationprocess; said method further comprising an electrode formation processof forming electrodes for connecting the exposed n-type and p-typethermoelectric semiconductor pieces to each other alternately and inseries after the thermoelectric semiconductor pieces exposure process,fabricating a provisional thermoelectric device, and thereafterperforming a process of fixedly attaching a heat radiation plate to oneof the surfaces of the provisional thermoelectric device, where theelectrodes are formed, and a heat absorption plate to the other via aninsulating fixture layer, respectively, and a process of removing theprovisional fixture layers either by heating or by use of a solventafter said preceding process.
 25. A method of fabricating athermoelectric device comprising: a grooved block fabrication process offorming two pairs of grooved blocks composed of an n-type thermoelectricsemiconductor and a p-type thermoelectric semiconductor, respectively,provided with a plurality of grooves formed at a same pitch and parallelwith each other, respectively, leaving a depthwise portion of respectivegrooved blocks intact; a first fitting process of fitting each pair ofthe grooved blocks composed of the n-type thermoelectric semiconductorand the grooved block of the p-type thermoelectric semiconductor, formedby said grooved block fabrication process, to each other such thatsurfaces with the grooves formed thereon face each other; a firstadhesion process of forming two integrated blocks by filling up gaps infitting parts between each pair of the grooved blocks composed of then-type thermoelectric semiconductor and the p-type thermoelectricsemiconductor, respectively, fitted to each other by said first fittingprocess, with adhesive insulation members, and solidifying the same; agrooving process of forming two grooved integrated blocks by forming ineach of the two integrated blocks a plurality of grooves at a same pitchand in the direction crossing the direction of the grooves formed bysaid grooved block fabrication process, leaving a depthwise portion ofrespective integrated blocks intact; a second fitting process of fittingthe two grooved integrated blocks to each other such that surfaces withthe grooves thus formed thereon face each other; a second adhesionprocess of forming a second integrated block by filling gaps in fittingparts between the two grooved integrated blocks fitted to each other bysaid fitting process with adhesive insulation members, and solidifyingthe same; and a thermoelectric semiconductor pieces exposure process ofexposing n-type and p-type thermoelectric semiconductor pieces byremoving all depthwise portions of the second integrated block, otherthan the fitting parts; characterized in that provisional fixture layersas insulation members for filing up gaps in the fitting parts are formedusing a material removable by heating or by use of a solvent in thefirst adhesion process or the second adhesion process; said methodfurther comprising an electrode formation process of forming electrodesfor connecting the exposed n-type and p-type thermoelectricsemiconductor pieces to each other alternately and in series after thethermoelectric semiconductor pieces exposure process, fabricating aprovisional thermoelectric device, and thereafter performing a processof fixedly attaching a heat radiation plate to one of the surfaces ofthe provisional thermoelectric device, where the electrodes are formed,and a heat absorption plate to the other via an insulating fixturelayer, respectively, and a process of removing the provisional fixturelayers either by heating or by use of a solvent after said precedingprocess.
 26. A method of fabricating thermoelectric device comprising: afirst grooving process applied to two n-type thermoelectricsemiconductor composite blocks prepared by bonding an n-typethermoelectric semiconductor block to a base, respectively, and twop-type thermoelectric semiconductor composite blocks prepared by bondinga p-type thermoelectric semiconductor block to a base, respectively, forforming a plurality of grooves at a same pitch, and to a depth close tothe interface between the respective thermoelectric semiconductor blocksand the base thereof, in the n-type thermoelectric semiconductor blockand the p-type thermoelectric semiconductor block, respectively; a firstfitting process of fitting the two pairs of the n-type thermoelectricsemiconductor composite block and the p-type thermoelectricsemiconductor composite block, with the grooves formed therein,respectively, by said first grooving process to each other,respectively, such that respective grooved surfaces face each other; afirst adhesion process of forming two integrated blocks by adhering thetwo pairs of the n-type thermoelectric semiconductor composite blocksand p-type thermoelectric semiconductor composite blocks to each other,respectively, by filling gaps in fitting parts between the respectiven-type thermoelectric semiconductor composite blocks and p-typethermoelectric semiconductor composite blocks, fitted to each other bysaid first fitting process, with adhesive insulation members; a secondgrooving process of forming two grooved integrated blocks by forming aplurality of grooves at a same pitch in the two integrated blocksformed, respectively, by said first adhesion process, in the directioncrossing the direction of the grooves formed by said first groovingprocess, and to a depth close to an interface between the respectivethermoelectric semiconductor blocks and the base thereof; a secondfitting process of fitting the two grooved integrated blocks to eachother such that respective grooved surfaces face each other; a secondadhesion process of forming a second integrated block by adhering thetwo grooved integrated blocks, fitted to each other by said secondfitting process, to each by filling in fitting parts between the twogrooved integrated blocks with adhesive insulation members; and athermoelectric semiconductor pieces exposure process of exposing n-typeand p-type thermoelectric semiconductor pieces by removing therespective bases of the second integrated block; characterized in thatprovisional fixture layers as insulation members for filing up gaps inthe fitting parts are formed using a material removable by heating or byuse of a solvent in the first adhesion process or the second adhesionprocess; said method further comprising an electrode formation processof forming electrodes for connecting the exposed n-type and p-typethermoelectric semiconductor pieces to each other alternately and inseries after the thermoelectric semiconductor pieces exposure process,fabricating a provisional thermoelectric device, and thereafterperforming a process of fixedly attaching a heat radiation plate to oneof the surfaces of the provisional thermoelectric device, where theelectrodes are formed, and a heat absorption plate to the other via aninsulating fixture layer, respectively, and a process of removing theprovisional fixture layers either by heating or by use of a solventafter said preceding process.